Green and Facile Fabrication of α-Zirconium Phosphate-Based Core–Multishell Nanoparticles for Enhancing Fire Retardant Performance of Poly(vinyl alcohol)
Zhihao Zhang,Zhongying Ma,Yuhua Wang
DOI: https://doi.org/10.1021/acsanm.0c01531
IF: 6.14
2020-08-14
ACS Applied Nano Materials
Abstract:At present, most flame retardants, especially halogenated compounds, are banned because of concern for environmental and health issues. In prospect of developing more ecofriendly and effective flame retardants, an alternative solution to develop novel biobased and inorganic flame retardants is addressed. Herein, a nano flame retardant consisting of a lamellar α-zirconium phosphate (α-ZrP) nanosheet modified with chitosan (CH), phytic acid (PA), and a metal ion (Cu<sup>2+</sup>) with a core–multishell structure is fabricated in water solution via a green and facile self-assembly method and applied to enhance the fire retardant effect of poly(vinyl alcohol) (PVA). Thermogravimetric analysis (TGA) demonstrated that after the addition of α@, PVA composites maintained their well-performed ability of char formation. The limit oxygen index (LOI) of pure PVA increased from 18.4 to 29.8% for PVA/α@ and it reached UL-94 V-1 grade. In the microscale combustion calorimeter test (MCC), the peak heat release rate (pHRR) and the total heat release (THR) of PVA/α@ sharply decreased by 82.3 and 62.2% compared with pristine PVA. The results implied that α@ could endow PVA with superior fire retardant properties. Moreover, the research manifested the synergy between α-ZrP and @Cu and a double barrier flame retardant mechanism in a condensed phase. In the α@ flame retardant system, the inorganic α-ZrP nanosheet acted as an insulating core, and the @Cu constituted an intumescent shell, where the outer @Cu intumescent shell formed an expanded char layer serving as the first barrier to hinder heat and oxygen transfer, and then the inner α-ZrP core layer, as the second barrier, would prevent the further exchange of flammable gases and energy between the polymer and fire during combustion. As a result, this ecofriendly nano flame retardant with the core–multishell structure has a potential application value.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.0c01531?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.0c01531</a>.XRD patterns of α-ZrP, @Cu, and α@ (Figure S-1); DTG curves of α-ZrP, @Cu, and α@ (Figure S-2); the XRD patterns of char residues of PVA/α-ZrP, PVA/@Cu, and PVA/α@ composites after vertical flame measurement (Figure S-3); the Raman spectrum of the char residues of pure PVA (Figure S-4); TGA data of α-ZrP, @Cu, α@, PVA, and PVA composites in N<sub>2</sub> (Table S-1); MCC data of all samples (standard deviations of three measurements are given in brackets) (Table S-2); flame retardant performance and smoke density of PVA and PVA composites (standard deviations of three measurements are given in brackets) (Table S-3); and the tensile strength of PVA and its composites (standard deviations of three measurements are given in brackets) (Table S-4) (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.0c01531/suppl_file/an0c01531_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology