Plasma driven exsolution of Ca as the adjacent dechlorinated site in La 0.8 Ca 0.2 MnO 3 perovskite: a highly mineralization chlorobenzene oxidation catalyst
Dan Tao,Yingying Qi,Shuangshuang Fu,Ning Yang,Kaixian Liu,Zekai Chen,Lu Li
DOI: https://doi.org/10.1016/j.apcata.2024.119784
IF: 5.723
2024-05-10
Applied Catalysis A General
Abstract:The degradation of chlorine-containing volatile organic compounds (CVOCs) utilizing catalytic combustion technology is subject to the catalyst chlorine poisoning, which is resulted from the chlorination of active phases, even though the structural stable perovskite. The reaction between Ca species and dissociated chlorine species is demonstrated as an efficient way to inhibited chlorine poisoning of the active phase. Herein, a Ca substituted partial La prepared La 0.8 Ca 0.2 MnO 3 (named as L8C2MO) perovskite was treated by 5% H 2 /Ar plasma driven route (the treated sample was denoted as L8C2MO-P), which was applied for the chlorobenzene oxidation removal. The integrated characterization results of XRD, XPS, HRTEM, etc . confirmed that Ca (mainly exhibited as CaCO 3 ) was successfully exsolved from La 0.8 Ca 0.2 MnO 3 and simultaneously leaved oxygen vacancies on the surficial layers. The continuous catalytic oxidation experiments illustrated that the conversion efficiency of L8C2MO was unexpectedly decreased compared with that of LaMnO 3 (LMO in short) sample, while that of L8C2MO-P was nearly maintained the oxidation capacity, with approximately 12°C of 90% chlorobenzene conversion temperature ( T 90 ) higher than that of LMO. Importantly, the CO 2 and inorganic chlorine species yields were significantly enhanced for L8C2MO and L8C2MO-P. The characteristic of used samples showed a possible chlorinated Ca species formation while the status of Mn phases was hardly changed, suggesting the exsolved Ca could inhibited the poison of Mn sites by binding with dissociative chlorine species. Additionally, oxygen vacancies that generated along with Ca exsolution process was definitely contributed to the deep oxidation of chlorobenzene. The possible reaction route was also studied by in situ DRITS and GCMS. The work provides a potential route as in situ growth of adjacent sites to protect active phases from chlorine poison in CVOCs catalytic oxidation process.
chemistry, physical,environmental sciences