Abstract:Few successes about butyl acrylate (BA) RAFT miniemulsion homopolymerization were reported, even though styrene, methyl methacrylate, and vinyl acetate had been successfully applied in reversible addition fragmentation transfer (RAFT) miniemulsion polymerization. In this article, four types of RAFT agent with various designed R and Z groups [benzyl dithioisobutyrate (BDIB), 1-phenylethyl phenyldithioacetate (PEPDTA), cumyl dithioisobutyrate (CDIB), benzyl dithiobenzoate] were used to mediate BA miniemulsion polymerization using the conditions (5 wt % hexadance and sodium dodecyl sulfate) effective for styrene and methyl methaerylate systems. All four types of the RAFT agents effectively control over the bulk polymerization. In contrast, only BDIB resulted in a rather narrow molecular weight distribution in the miniemulsion polymerization. A pronounced inhibition and rate retardation were observed in both bulk and miniemulsion polymerizations mediated by CDIB and benzyl dithiobenzoate. When compared with the bulk polymerization, a much longer inhibition period (over eight times) was observed in the CDIB-mediated. miniemulsion polymerization. It was concluded that only the RAFT agent with the primary R group and Z group with less stabilizing ability to the intermediate radicals is effective to mediate BA miniemulsion polymerization in terms of achieving a narrow molecular weight distribution and short inhibition period. (C) 2007 Wiley Periodicals, Inc.

Influence of Comonomers on the Transformation of MBA Gel Fibers into Polymer Micro tubes via RAFT Polymerization

Tailoring Polymer Molecular Weight Distribution and Multimodality in RAFT Polymerization Using Tube Reactor with Recycle

INFLUENCE OF MONOMER COMPOSITION ON THE CHAIN TRANSFER COEFFICIENT IN METHYL METHACRYLATE/BUTYL ACRYLATE RAFT COPOLYMERIZATION

Modeling and Experimentation of RAFT Solution Copolymerization of Styrene and Butyl Acrylate, Effect of Chain Transfer Reactions on Polymer Molecular Weight Distribution

Toward Understanding of Branching in RAFT Copolymerization of Methyl Methacrylate Through a Cleavable Dimethacrylate

Semibatch RAFT Polymerization for Branched Polyacrylamide Production: Effect of Divinyl Monomer Feeding Policies

Synthesis and characterization of hyperbranched polyacrylamide using semibatch reversible addition-fragmentation chain transfer (RAFT) polymerization

Influence of Small Amount of Co-Monomers on Acrylonitrile Polymerization in Dimethylformamide (DMF) Solution

Modeling of Branching and Gelation in RAFT Copolymerization of Vinyl/Divinyl Systems

Preparation of polymer microtubes via RAFT polymerization of N, N'-methylene bisacrylamide gel fibers

Fabrication of Fluoropolymer Microtubes Via RAFT Copolymerization of N,N'-Methylene Bisacrylamide Gel Fibers and Fluoromonomer.

Preparation of Polymer Microtubes Via RAFT Polymerization of Sole MBA Xerogel Fibers

RAFT miniemulsion polymerization of methyl methacrylate

RAFT Ab Initio Emulsion Copolymerization of Γ-Methyl-α-methylene-γ-butyrolactone and Styrene

Kinetics and modeling of semi-batch RAFT copolymerization with hyperbranching

Butyl Acrylate RAFT Polymerization in Miniemulsion

Kinetics of methyl methacrylate and n-butyl acrylate copolymerization mediated by 2-cyanoprop-2-yl dithiobenzoate as a RAFT agent

Direct Transformation of N,N '-Methylene Bisacrylamide Self-Assembled Fibers into Polymer Microtubes Via Raft Polymerization

Effect of Monomer Composition on Apparent Chain Transfer Coefficient in Reversible Addition Fragmentation Transfer (raft) Copolymerization

Reversible Addition–fragmentation Transfer (RAFT) Copolymerization of Methyl Methacrylate and Styrene in Miniemulsion

Reversible addition–fragmentation chain transfer polymerization of methyl methacrylate in emulsion