Abstract:Multi - walled carbon nanotubes with diameters of 20 similar to 30nm were synthesized by cobalt - catalytic decomposition of acetylene, which are showed by TEM images. A series of pretreatments including purification, annealing and doping were performed before carrying out hydrogen storage experiments at room temperature and modest pressure ( 12 MPa). For comparison, the annealing treatments were processed under ambient pressure in air and nitrogen atmosphere respectively. KNO3 solutions (0.1 mol/L and 1.0 mol/L) were used to dope carbon nanotubes. The results suggest that both annealing and doping play an important role in the hydrogen storage capacity of carbon nanotubes. Under the same conditions conducted, MWNTs annealed in nitrogen adsorbed more hydrogen than those annealed in air. FTIR spectra of the samples shows that the amount of oxygen functional groups linked to MWNTs after annealed in air is more than that treated in nitrogen. The former treatment may bring about more agglomeration of MWNTs, decrease the specific area and surface activity of MWNTs and eventually lead to lower capacity of hydrogen adsorption. The results also show that with the same dopant, the capacity of hydrogen adsorption has great difference when the concentration of the doping solution changed. Hydrogen adsorption of MWNTs increased not only after doped in KNO3 solution but also with the increase of solution concentration in certain extent. An optimal result(3.2%) was obtained when carbon nanotubes were annealed in nitrogen at 500 degreesC and doped in 1.0 mol/L KNO3 solution. Hydrogen desorption experiments were also carried out at room temperature. It is found that after a typical adsorption/desorption cycle under ambient. temperature, the MWNTs samples still retain significant amount of stored hydrogen. The phenomenon may be attributed to the existence of two types of adsorbed hydrogen in the structure: physical and chemical adsorptions, the former can be released easily and the latter is strongly bound and could be released more difficultly.

Hydrogen uptake in multi walled carbon nanotubes at room temperature

THE EFFECT OF SURFACE TREATMENTS ON HYDROGEN STORAGE OF CARBON NANOTUBES

Hydrogen Uptake by Carbon Nanotubes

Pore Structure And Hydrogen Storage Of Carbon Nanotubes

Hydrogen Adsorption of Open-Tipped Insufficiently Graphitized Multiwalled Carbon Nanotubes

Hydrogenation of single-walled carbon nanotubes

Hydrogen Storage in Carbon Nanotubes Through the Formation of Stable C-H Bonds.

Hydrogen Adsorption in Bundles of Well-Aligned Carbon Nano Tubes at Room Temperature

Hydrogen Storage in Multi-Wall Carbon Nanotubes Using Samples Up to 85 G

Effects of structure and surface properties on carbon nanotubes’ hydrogen storage characteristics

Hydrogen Storage Capacity of Single-Walled Carbon Nanotube Prepared by A Modified Arc Discharge

Hydrogen Storage in Heat-Treated Carbon Nanofibers Prepared by the Vertical Floating Catalyst Method

Abstract Submitted for the MAR07 Meeting of The American Physical Society Temperature and Pressure Dependence of Hydrogen Coverage on Single-Walled Carbon Nanotubes1

Research Progress of Hydrogen Storage in Carbon Nanotubes

Studies of Multi-walled Carbon Nanotubes and Their Capabilities of Hydrogen Adsorption

The Effect of Pretreatments on Hydrogen Adsorption of Multi-Walled Carbon Nanotubes

Preparation of Large Amounts of Carbon Nanotubes in Hydrogen Atmosphere by Arc-Discharge

Hydrogen Storage Behavior of Amorphous Carbon Nanotubes at Low Pressure and Room Temperature

HYDROGEN ADSORPTION BEHAVIOR OF CARBON NANOTUBES WITH DIFFERENT STRUCTURE

Hydrogen Storage Capacity Of Potassium-Doped Multi-Walled Carbon Nanotubes

Theoretical Study on the Adsorbed Hydrogen Molecules on Multi-Walled Carbon Nanotubes