Direct Observation of Global Elastic Intervalley Scattering Induced by Impurities on Graphene
Can Wang,Huaiqiang Wang,Wang Chen,Xuedong Xie,Junyu Zong,Lulu Liu,Shaoen Jin,Yongheng Zhang,Fan Yu,Qinghao Meng,Qichao Tian,Li Wang,Wei Ren,Fangsen Li,Haijun Zhang,Yi Zhang
DOI: https://doi.org/10.1021/acs.nanolett.1c02714
IF: 10.8
2021-09-27
Nano Letters
Abstract:The scattering process induced by impurities in graphene plays a key role in transport properties. Especially, the disorder impurities can drive the ordered state with a hexagonal superlattice on graphene by electron-mediated interaction at a transition temperature. Using angle-resolved photoemission spectroscopy (ARPES), we reveal that the epitaxial monolayer and bilayer graphene with various impurities display global elastic intervalley scattering and quantum interference below the critical temperature (34 K), which leads to a set of new folded Dirac cones at the Brillouin-zone center by mixing two inequivalent Dirac cones. The Dirac electrons generated from intervalley scattering without chirality can be due to the breaking of the sublattice symmetry. In addition, the temperature-dependent ARPES measurements indicate the thermal damping of quantum interference patterns from Dirac electron scattering on impurities. Our results demonstrate that the electron scattering and interference induced by impurities can completely modulate the Dirac bands of graphene.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.nanolett.1c02714.Details of methods; RHEED patterns and room temperature STM images of pristine ML and BL graphene (Figure S1); RHEED patterns, room temperature STM images, and ARPES band dispersion of sub-ML WSe2 and MoSe2 on graphene (Figure S2); RHEED pattern, room/low temperature STM image, and XPS spectrum of Nb cluster on graphene (Figures S3 and S4); replica Dirac cone in graphene with W cluster and air-exposed samples (Figure S5); saddle point at M′ for ML and BL graphene with Nb cluster (Figure S6); tight-binding calculation and DFT band structures of pristine graphene and -period superlattice graphene (Figure S7); Fermi velocity at the Γ point obtained by νF = (1/ℏ)(∂E/∂k) (Figure S8); temperature-dependence EDCs arond Γ point and MDCs at the Dirac point for the folded Dirac cones (Figure S9); strain effects on -period superlattice graphene (Figure S10) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology