Segmented Poly(Ether Ester Amide) Copolymers As Scaffolds for Tissue Engineering

AA Deschamps,DW Grijpma,J Feijen

IF: 11.467

2002-01-01

Journal of Controlled Release

Abstract:s / 87 (2003) 199–308 303 Table 1 Results of PEEA polymerizations Feed PEO content Actual soft to Actual PEO [ h] b composition in feed hard segment content dL/g a a (wt%) ratio (wt%) PEA 0 0/100 0 0.64 300 PEEA 70/30 35 65/35 32 0.51 300 PEEA 55/45 27 49/51 24 0.55 300 PEEA 30/70 15 25/75 12 0.68 1000 PEEA 70/30 54 76/24 58 0.56 1000 PEEA 55/45 42 57/43 44 0.64 1000 PEEA 30/70 23 32/68 25 0.77 4000 PEEA 70/30 65 71/39 66 0.64 4000 PEEA 55/45 51 61/39 57 0.69 4000 PEEA 30/70 28 34/66 31 0.53 a 1 As determined by H-NMR. b Determined in CHCl /MeOH (1:1 v:v) at 25 8C. 3 Results PEEA segmented copolymers of different compositions (Table 1) have been evaluated as possible scaffold materials for tissue engineering. PEEA copolymers are microphase separated and up to four thermal transitions can be observed by DSC. Phase separation in the system is enhanced by increasing the molecular weight of starting poly(ethylene glycol) (PEG). The mechanical properties, swelling characteristics and degradation rates of the copolymers are influenced by the phase separation. By changing the PEEA composition, tensile strengths can be varied from 4 to 40 MPa and elongations at break from 100 to 800%. Water-uptake ranges from 6 to a high value of 340% (Fig. 2). PEEA scaffolds with a porosity of 90% could be prepared by molding of the copolymer and subsequent salt-leaching (Fig. 3). Endothelial cells were cultured on PEA, 300 PEEA 30/70 and 1000 PEEA 30/70. All copolymers sustained cell attachment and growth. The most abundant cell growth was found on the PEA polymer, which does not contain PEO. Higher PEO contents lead to a decrease in cell attachment and growth. The in vivo degradation of PEEA copolymers is currently being studied. Fig. 2. Water-uptake as a function of soft segment content for PEEA prepared from PEG 300 ( d), PEG 1000 ( h) and PEG 4000 ( m). 304 Abstracts / 87 (2003) 199–308 Fig. 3. Porous scaffold prepared from 300 PEEA 55/45 (pore sizes: 500–710 mm, porosity: 90%). Conclusions The physical properties and the degradability make PEEA copolymers good materials for use in medicine. Endothelial cells have been shown to attach and grow on PEEA copolymers. These copolymers are processable into highly porous scaffolds, which make them suitable materials for tissue engineering. Acknowledgements The authors thank IsoTis, Bilthoven for their financial contribution and Ype van der Zijpp for his help in the culture and seeding of the cells. References [1] R. Langer et al., Science 260 (1993) 920–926. [2] J.M. Bezemer et al., J. Biomed. Mater. Res. 52 (2000) 8–17. PREPARATION OF INTERCONNECTED HIGHLY POROUS POLY(D,L-LACTIDE) STRUCTURES BY SUGAR TEMPLATING AND FREEZE-DRYING Q. Hou, D.W. Grijpma, J. Feijen Institute for Biomedical Technology (BMTI), Department of Polymer Chemistry and Biomaterials, Faculty of Chemical Technology, University of Twente, P.O. Box 217, 7500AE, Enschede, The Netherlands Introduction Tissue engineering aims at developing functional substitutes for damaged or diseased tissues, and has attracted much attention since the last decade [1–3]. In tissue engineering, three-dimensional biodegradable polymeric scaffolds play an important role as active, temporary supports for the transplantation of specific tissue cells. Besides the chemical composition of the scaffolding material, careful design of the microstructure and morphology of the porous structures is of critical importance for their success. In general, a high porosity of the scaffold is desired in order to obtain a large specific area for cell attachment and tissue in-growth. Furthermore, the pore morphology can affect the growth of cells and even alter cell function [4]. Interconnected pores larger than the dimensions of the cells are essential for allowing infiltration of the cells into the scaffold, whereas smaller pores may influence the exchange