Laser Heat Treatment of Low-Alloy Ultrahigh-Strength Steel Laser-Welded Joints

C. Luo,Y. Cao,L. Zhao,J. Shan

DOI: https://doi.org/10.29391/2019.98.020

IF: 2.2

2019-01-01

Welding Journal

Abstract:The poor bending property of laser-welded joints limits the application of low-alloy ultrahigh-strength steel (LAUHSS). In this work, two stages of laser heat treatment (LHT) were performed to enhance the face- and back-bending property of joints with minimized strength loss. The microstructures and mechanical properties were evaluated, and the influence mechanism of LHT on the bending property was discussed. The first LHT aimed to improve the back-bending property, after which the joints were comprised of the austenized and tempering zones. In the tempering zone, the original inhomogeneous microstructures transformed into similar tempered martensite. This smoothed out the steep hardness gradient to relatively uniform values. In the austenized zone, austenization occurred and the hardness valley still existed around the sides of the zone. The mechanical property test results showed the back-bending angle could be improved from 30 deg to more than 90 deg, while the face-bending angle showed unsatisfactory results with more than 1280 MPa tensile strength. The second LHT was performed based on the first LHT to improve the face-bending property of joints. With lower power in the second LI-It the dual-phase microstructures in the austenized zone tempered. Additionally, the hardness distributions of joints tended to be more uniform without valleys. A more than 90-deg face-bending angle and about 1205 MPa tensile strength were obtained. After LHT, the range of plastic deformation during the bending process expanded instead of concentrating in the hardness valley zone, which led to a larger relative bending radius and less tensile stress on the bending surface. This is beneficial for the improvement of the bending property.