Thermal conductivity of 3d graphene filled polymer composite

Yun-Hong Zhao,Zhen-Kun Wu,Ya-Fei Zhang,Shu-Lin Bai

2015-01-01

Abstract:Graphene foam (GF), graphene sheet (GS) and carbon black (CB) were filled into polydimethylsiloxane (PDMS) to make novel polymer composites. The thermal properties of those composites were investigated. It is found that at 0.5 and 0.7 wt% graphene foam, the thermal conductivity of GF/PDMS composites increases from 0.40 to 0.56 Wm -1 K -1 , which are 200-300% that of pure PDMS, and about 20% higher than that of GS/PDMS composite. Furthermore, the adding of CB into the space of GF network and the interior of GF arms reinforces the thermal transportation, manifested by the increased thermal conductivity with 6 wt% CB. The coefficient of thermal expansion of 0.7 wt% GF/PDMS is (80-137)×10 -6 /K within 30-150 o C, much lower than those of 0.7 wt% GS/PDMS composite and pure PDMS. In addition, thermal stability of 0.7 wt% GF/PDMS composite is superior over 0.7 wt% GS/PDMS composite, and they are further improved by CB adding. All above results demonstrate that the GF filled polymer composite is a good candidate for thermal interface materials.