Microstructural And Reactivity Changes Of Coal Char During Steam Gasification At Low-Medium Temperature

Jingbiao Yang,Ningsheng Cai,Zhenshan Li

2007-01-01

Abstract:The purpose of this study is to investigate the relationship between the steam gasification reactivity of a Chinese lignite char (raw-char) and char generated from raw coal loaded with potassium carbonate (K-char) and microstructural changes. Steam gasification of the raw-char and the K-char was performed in a fixed bed reactor. After gasification, the gasified chars at different carbon conversions were examined using X-ray diffraction (XRD), and the XRD patterns of raw-char at various conversions showed that as gasification proceeded, the graphitization degree of raw-char increased with an increase in carbon conversion. On the other hand, the microstructure of carbon of K-char could not be detected by XRD due to the surface of K-char was covered with dense K2CO3 dispersing uniformly on it. It was revealed;hat laser Raman spectroscope (RS) and a scanning electron microscope combined with an energy dispersive X-ray spectrometer (SEM/EDX) were very effective for the comprehensive evaluation of carbonaceous structure evolution during gasification. The SEM images of the raw-char showed that porous structure with rough surface and structure of well organized, longitudinal tubes coexisted, but in the case of K-char, only porous structure with rough surface was observed during steam gasification. The Raman spectra of raw char at different carbon conversions showed that the disordered carbon having higher reactivity than the graphitic carbon was gasified preferentially and as a result the ratio of graphitic carbon increased. Graphitic carbon and disordered carbon of K-char were consumed simultaneously at the same rate during K-catalyzed steam gasification due to uniformly dispersion of K2CO3 in the char matrix and, redistribution and penetration of potassium compounds through the pores of the K-char matrix during gasification.