Abstract:a, Key Laboratory of Material Chemistry for Energy Conversion and Storage (Huazhong University of Science and Technology), Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan, 430074, P.R. China. *Email: wangdl81125@hust.edu.cn b, Center for Functional Nanomaterials, Brookhaven National Laboratory, Upton, NY, USA Graphene, a single-atom-thick hexagonally arrayed sp2 carbon atoms bonded sheet, has attracted tremendous interest in renewable energy conversion and storage devices due to its extraordinary properties, especially ultrahigh specific surface area and predominant electron conductivity1. However, graphene based two-dimensional catalysts suffer from an irreversible re-stacking of the nanosheets due to the strong π-interaction during thermal annealing process and electrochemical measurements which would result in a lower surface area, limiting the mass transfer rate and even decreasing the catalytic activity as well as electrochemical stability. Figure 1 (a) TEM image of NSGCB; (b) ORR activity of NSGCB and the corresponding comparative catalysts; (c) TEM image of NSCNT-3; (d) ORR activity of NSCNT-3 and the corresponding comparative catalysts. Herein, we report two strategies for the synthesis of nitrogen and sulfur co-doped three-dimensional graphene intercalated structure nanomaterials as electro-catalysts for ORR in alkaline medium. One is the insertion of Vulcan XC-72 carbon spheres into the graphene layer, forming a graphene-Vulcan XC-72- grapheme “sandwich-like” structure2. The other way is partially unzipping of multi-walled carbon nanotubes to form a graphene nanoribbon-carbon nanotube-graphene nanoribbon structure. Both of the prepared three-dimensional structured nanocomposites were experienced to nitrogen and sulfur co-doping process, and moreover, the resulting doped electro-catalysts exhibited outstanding ORR performance. Acknowledgements This work was supported by the National Natural Science Foundation (21306060, 21573083), the Program for New Century Excellent Talents in Universities of China (NCET-13-0237), the Doctoral Fund of Ministry of Education of China (20130142120039). References (1) Li, Y., Zhao, Y., Cheng, H., Hu, Y., Shi, G., Dai, L., & Qu, L. Nitrogen-doped graphene quantum dots with oxygen-rich functional groups. Journal of the American Chemical Society, 2011, 134, 15-18. (2) Wu, M., Wang, J., Wu, Z., Xin, H. L., & Wang, D. Synergistic enhancement of nitrogen and sulfur co-doped graphene with carbon nanosphere insertion for the electrocatalytic oxygen reduction reaction. Journal of Materials Chemistry A, 2015, 3, 7727-7731. Figure 1

Three-Dimensional Nitrogen-Doped Graphene/Mno Nanoparticle Hybrids As A High-Performance Catalyst for Oxygen Reduction Reaction

Three-Dimensional Nitrogen-Doped Graphene/MnO Nanoparticle Hybrids as a High-Performance Catalyst for Oxygen Reduction Reaction

Electrochemical doping of three-dimensional graphene networks used as efficient electrocatalysts for oxygen reduction reaction.

Sulfur and Nitrogen Co-Doped, Few-Layered Graphene Oxide As A Highly Efficient Electrocatalyst for the Oxygen-Reduction Reaction

Low-Loading Cobalt Coupled With Nitrogen-Doped Porous Graphene As Excellent Electrocatalyst For Oxygen Reduction Reaction

Hierarchical Hybrid of Ni 3 N/N-doped Reduced Graphene Oxide Nanocomposite As a Noble Metal Free Catalyst for Oxygen Reduction Reaction

Noble-Metal-Free Iron Nitride/Nitrogen-Doped Graphene Composite for the Oxygen Reduction Reaction

Mn Doping of Cobalt Oxynitride Coupled with N-rGO Nanosheets Hybrid As a Highly Efficient Electrocatalyst for Oxygen Reduction and Oxygen Evolution Reaction

An Effective Poly(p-Phenylenevinylene) Polymer Adhesion Route Toward Three-Dimensional Nitrogen-Doped Carbon Nanotube/reduced Graphene Oxide Composite for Direct Electrocatalytic Oxygen Reduction

Nico2o4/N-Doped Graphene As an Advanced Electrocatalyst for Oxygen Reduction Reaction

Nitrogen-doped Mesoporous Graphene As a Synergistic Electrocatalyst Matrix for High-Performance Oxygen Reduction Reaction.

Co3O4@g-C3N4 Supported on N-doped Graphene As Effective Electrocatalyst for Oxygen Reduction Reaction

Multiple Metal (cu, Mn, Fe) Centered Species Simultaneously Combined Nitrogen‐doped Graphene As an Electrocatalyst for Oxygen Reduction in Alkaline and Neutral Solutions

Nitrogen-doped Graphene Derived from Ionic Liquid As Metal-Free Catalyst for Oxygen Reduction Reaction and Its Mechanisms

A Three-Dimensionally Structured Electrocatalyst: Cobalt-Embedded Nitrogen-Doped Carbon Nanotubes/Nitrogen-Doped Reduced Graphene Oxide Hybrid for Efficient Oxygen Reduction.

Graphitic-N-rich N-doped graphene as a high performance catalyst for oxygen reduction reaction in alkaline solution

Nitrogen-doped graphene prepared by a transfer doping approach for the oxygen reduction reaction application

Nitrogen-doped Graphene Aerogel-Supported Spinel CoMn2O4 Nanoparticles As an Efficient Catalyst for Oxygen Reduction Reaction

Highly Efficient Nitrogen and Sulfur Co-Doped Three-Dimensional Graphene-Based Nanocatalysts for the ORR

Highly Dispersed and Small-Size Pd–Cu Nanoparticles Supported on N-Doped Graphene for Oxygen Reduction Reaction Catalysts

Efficient Oxygen Reduction Electrocatalysis on Mn3O4 Nanoparticles Decorated N-doped Carbon with Hierarchical Porosity and Abundant Active Sites