Influence Of Processing Parameters On The Microstructure Of Tc4 Titanium Alloy By Laser Micro Cladding Deposition Manufacturing

Yao,B,Lin,F,Ma,XL

2016-01-01

Rare Metal Materials and Engineering

Abstract:In the process of laser micro cladding deposition manufacturing of TC4, the influence of the laser power and scanning speed on the microstructure and micro-hardness were analyzed. The results indicate that the prior beta columnar grains dominate the entire cladding layer or the columnar are epitaxial growth with a thin layer of fine dendritic microstructure in the top. There are two regions, bright region and dark region in the macrostructure. When P/V is less than 40 W.s.mm(-1), the bright region is in the top and the dark region is below it. The microstructure of the two regions is acicular martensite and it is finer in bright region than in dark region. The micro-hardness of the bright region is higher than that of the dark region. With the increase of the laser power or the decrease of the scanning speed, the height of the bright region increases and the micro-hardness of the bright and dark regions all decreases. Otherwise, the bright region is under the dark region. In this case, the microstructure of the bright region is still acicular martensite, while the microstructure of the dark region is coarsened from acicular martensite by a solution and aging treatment of the repeated heating; at the same time, the micro-hardness of the dark region is higher than the bright region.