Effects of Deformation Parameters on the Superplastic Behavior and Microstructure Evolution of TA32 Alloy

Liu Zhangguang,Li Peijie,Yin Xiyue,Wu Fengyong,Xiong Liangtong,Gao Haitao

2018-01-01

Abstract:High-temperature tensile tests in the deformation temperature range of 895 similar to 935 degrees C and strain rate range of 8.3x10(-4)similar to 1.32x10(-2) s(-1) were conducted for TA32 high-temperature titanium alloy developed independently by China, and electron back-scattered diffraction (EBSD) technique was used to characterize grain morphology, orientation, and grain distribution. The results show that TA32 alloy provides superior superplastic deformation capability, with a maximum elongation up to 1141.8%. At high temperature and low strain rate, the growth of grains tends to raise the true stress at late deformation stages. Both the true stress and elongation are sensitive to deformation temperature and strain rate, and dynamic recrystallization is more likely to occur in high temperature or low strain rate conditions. Under different deformation conditions of superplastic tension, dynamic recrystallization occurs. After deformation, the textures nearly exhibit random orientations, and the original grains are equiaxed with better dimensional uniformity. During the deformation process, discontinuous dynamic recrystallization serves as the dominant dynamic recrystallization mechanism. With the increase in deformation temperature, decrease in the strain rate, and increase in deformation degree, discontinuous dynamic recrystallization plays a more important role, while continuous dynamic recrystallization weakens.