Experimental Investigation of the Phase Equilibria of the Zn-Al-Zr Ternary System at 723 K (450 °C)
Liangping Chen,Fucheng Yin,Xuemei Ouyang,Manxiu Zhao,Zhi Li
DOI: https://doi.org/10.1007/s11661-015-3125-8
2015-01-01
Abstract:Based on the techniques of scanning electron microscopy equipped with energy dispersive X-ray spectroscopy, X-ray powder diffraction, and Electron probe microanalysis (EPMA), the 723 K (450 °C) isothermal section of the Zn-Al-Zr ternary system has been determined using equilibrated alloy method with the aid of diffusion couple approach. The ternary compound Zn 50 Al 25 Zr 25, named T phase in the present work, is confirmed to be stable at 723 K (450 °C), and it has a very large composition rang of Zn from 11.9 to 58.5 at. pct. The T phase is in equilibrium with all the binary phases except Zr 3 Al, Zr 2 Al, ZnZr, and Zn 2 Zr. The maximum solubility of Zn in ZrAl 3 , Zr 2 Al 3 , ZrAl, Zr 4 Al 3 , Zr 3 Al 2 , Zr 2 Al, and Zr 3 Al is 2.8 (measured by EDS), 1.00, 1.17, 0.82, 0.48, 0.78, and 1.52 (measured by EPMA) at. pct, respectively. The maximum solubility of Al in ZnZr, Zn 2 Zr, and Zn 3 Zr is 10.3, 3.9 and 10.44 at. pct, respectively.