Experimental study on seismic behavior of assembled monolithic beam-column interior joints with rebar spliced by pressed sleeve

ZHAO Zuozhou,HAN Wenlong,QIAN Jiaru,LIU Shiwei,WANG Yueyuan

DOI: https://doi.org/10.14006/j.jzjgxb.2017.04.006

2017-01-01

Abstract:To study the seismic behavior of assembled monolithic beam-column interior joints with rebar spliced by pressed sleeve,quasi-static tests of two assembled monolithic interior joints and one cast-in-place interior joint were carried out.The crack and failure process of the specimens were observed.Further analysis was conducted to investigate the seismic behavior,such as the hysteretic characteristic,bearing capacity,deformation capacity,and rebar strain development process.The test results indicate that specimens with shear failure in the joint core area or flexural failure at the beam fixed end all fail in the expected failure modes.The failure process,crack patterns and major seismic behavior indexes of the assembled monolithic joint and the cast-in-place joint with the expected shear failure in the joint core area are basically consistent.The measured load-carrying capacity of the assembled monolithic joints,which fail in shear mode in the joint core area and flexural mode at the beam fixed end,respectively are 1.62,1.31 times as large as the calculated capacity according to the formulas in the current design code.The equivalent ultimate inter-story drift ratios of the precast assembled monolithic joints are 1/26 and 1/27.After the test and removal of concrete,no cracks and rebar slippage were observed at the sleeve,indicating that the pressed sleeve splice can transfer the tensile and compressive force of rebars effectively.