La-doped Titania Nanocrystals with Superior Photocatalytic Activity Prepared by Hydrothermal Method

Yanchao JIAO,Mingfeng ZHU,Feng CHEN,Jinlong ZHANG

DOI: https://doi.org/10.1016/s1872-2067(11)60483-x

IF: 16.5

2013-01-01

Chinese Journal of Catalysis

Abstract:Potassium titanate (KTO) nanobars were synthesized by a hydrothermal method and used as a precursor to synthesize TiO2 nanocrystals. La doping of the TiO2 nanocrystals was achieved by introducing La3+ into the hydrothermal media. The hydrothermal transition of KTO to TiO2 was investigated under various conditions, finding that the pH of the hydrothermal media, the temperature, and the pre-treating procedure play important roles in the phase transition. X-ray diffraction and transmission electron microscopy were used to characterize the crystal phase and morphology of the samples and the transition process of the hydrothermal reaction. The content of La3+ in the samples was measured by inductively coupled plasma atomic emission spectroscopy. The photocatalytic activity of the La-doped TiO2 (LaT) was measured under UV light with the degradation of methyl orange (MO, 10 mg/L). The results showed that the photocatalytic activity of TiO2 was enhanced remarkably by La-doping. LaT hydrothermally prepared with 0.15 mol/L La3+ at under 180 °C showed the optimal reaction constant of 0.11 min−1 for the degradation of MO, about 9.20 and 3.69 times than those of bare TiO2 and P25, respectively.