Abstract:The corrosion phenomenon and its economic impacts can hardly be ignored in any application. This study synthesized a quaternary ammonium salt (3) containing hydrophobic dodecyl and electron-rich diallylbenzyl amine moieties to be used in 15 % HCl as a corrosion inhibitor of mild steel. Several techniques, such as 1H and 13C NMR, IR, TGA, and elemental analysis, have been used to characterize inhibitor 3. Popular corrosion measurement techniques, namely weight loss, potentiodynamic polarization techniques, and electrochemical impedance spectroscopy, have been used to determine the efficiency of inhibitor 3. At 303 K and a moderately low concentration of 50 ppm, the quaternary ammonium salt-based inhibitor demonstrated a maximum efficiency of ≈95.0 %. At elevated temperatures of 313, 323, and 333 K, the inhibition efficacy values were recorded as 91.3, 82.8, and 75.0 %, respectively. Adsorption isotherm study revealed that the adsorption of inhibitor 3 followed Langmuir adsorption isotherm. The value of Δ G a d s ° was found to be - 40.19 kJ mol-1, indicating that inhibitor 3 became adsorbed via a mixed physi-chemisorption mechanism. A very high adsorption constant ( K a d s ) of 1.53 × 105 L mol-1 suggested strong adsorption of inhibitor 3. The difference in activation energy ( E a ) value of 42.4 kJ mol-1 between the control and the inhibited solution indicated an efficient adsorption of inhibitor 3. The ability of inhibitor 3 to retard both anodic and cathodic half-cell reactions was proved via open circuit potential and Tafel curves studies. Detailed discussions on the change in corrosion current densities ( i c o r r ), polarization ( R p ) and charge transfer ( R c t ) resistances have been offered to discuss the inhibition efficiency. Water contact angle measurement showed a drastic increase in mild steel surface hydrophobicity following inhibitor 3 adsorption. SEM-EDX and XPS studies confirmed the definitive presence of inhibitor 3 on the mild steel surface. Density functional theory (DFT) studies revealed the frontier molecular orbitals with which the metal surface interacts. A detailed corrosion inhibition mechanism has been offered in the context of adsorption isotherm and DFT studies.

A Newly Synthesized Green Corrosion Inhibitor Imidazoline Derivative for Carbon Steel in 7.5% NH4Cl Solution

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

New and Green Corrosion Inhibitor Based on New Imidazole Derivate for Carbon Steel in 1 M HCl Medium: Experimental and Theoretical Analyses

A New Imidazole Derivative for Corrosion Inhibition of Q235 Carbon Steel in an Acid Environment

A Novel Imidazoline Derivative As Corrosion Inhibitor for P110 Carbon Steel in Hydrochloric Acid Environment

Experimental and theoretical studies for corrosion inhibition of carbon steel by imidazoline derivative in 5% NaCl saturated Ca(OH)2 solution

Long Chain Imidazole Derivative As a Novel Corrosion Inhibitor for Q235 Steel in 15 % HCl Medium under Hydrodynamic Condition: Experimental and Theoretical Examinations

Electrochemical, Chemical and Theoretical Exploration of the Corrosion Inhibition of Carbon Steel with New Imidazole-Carboxamide Derivatives in an Acidic Environment

Comprehensive Analysis of the Effect of New Efficient and High Temperature Resistant Imidazoline Derivatives on the Corrosion Inhibition Performance of Q235: Experimental and Theoretical Studies

Synthesis of a new quaternary ammonium salt for efficient inhibition of mild steel corrosion in 15 % HCl: Experimental and theoretical studies

The Inhibition Mechanism of Imidazoline Phosphate Inhibitor for Q235 Steel in Hydrochloric Acid Medium

Experimental and theoretical investigations of a novel imidazoline quaternary ammonium salt as an effective inhibitor of Q235 steel in 1 M HCl

Corrosion Inhibition of Q235 Steel by A Novel Imidazoline Compound under H2s and Co2 Coexistence

Corrosion Inhibition of Mild Steel by Bromide-Substituted Imidazoline in Hydrochloric Acid

Experimental and Quantum Chemical Studies of a Green Corrosion Inhibitor for Mild Steel in Acidic Chloride Solution

Preparation and Application of Modified Imidazole with MPEG (polyethylene Glycol Monomethyl Ether) As Carbon Steel Inhibitor

Corrosion Inhibition Of Mild Steel By The Hydrolysate Of An Imidazoline-Based Inhibitor In Co2-Saturated Solution

Electrochemical, Surface Analysis, and Theoretical Investigation of 3-Hydroxy-5-(phenylamino)-4-(p-tolyldiazenyl)thiophen-2-yl)(phenyl)methanone As a Corrosion Inhibitor for Carbon Steel in a Molar Hydrochloric Acid Solution

Experimental and Computational Approach on the Development of a New Green Corrosion Inhibitor Formulation for N80 Steel in 20% Formic Acid.

A Glycine Derivative As Corrosion Inhibitor for Carbon Steel in 3.5 Wt% NaCl Solution: the Combined Experimental and Theoretical Calculation

Electrochemical, Surface and Quantum Chemical Studies of Novel Imidazole Derivatives As Corrosion Inhibitors for J55 Steel in Sweet Corrosive Environment