Abstract:The Ni‐boride/phosphide particles anchored amorphous B‐doped carbon layer with hierarchical porous characteristics in Ni foam (Ni3P/Ni3B/B−C/NF) was constructed for overall water splitting. Benefitting from the synergistic effect between Ni3P and Ni3B, the amorphous B−C layer and high space utilization of NF, the Ni3P/Ni3B/B−C/NF electrocatalyst exhibited a desirable activity and durability for water electrolysis. The rational design of efficient and economical bifunctional electrocatalysts remained a challenge for overall water electrolysis. In this work, the Ni‐boride/ phosphide particles anchored amorphous B‐doped carbon layer with hierarchical porous characteristics in Ni foam (Ni3P/Ni3B/B−C/NF) was fabricated for overall water splitting. The Boroncarbide (B4C) power was filled and fixed in the NF interspace through the electroplating and electroless plating, and then annealed in vacuum high temperature. The amorphous B−C layer derived from the B4 C not only speeded up the electron transport, but also cooperate with Ni‐boride/phosphide to enhance the electrocatalytic activity for HER and OER synergistically. Furthermore, the hierarchical porous architecture of Ni3P/Ni3B/B−C/NF increased space utilization to load more active materials. The self‐supported Ni3P/Ni3B/B−C/NF electrode possessed a low overpotential of 212 and 280 mV to deliver 100 mA cm−2 for HER and OER, respectively, and high stability for 48 h. In particular, the electrolyzer constituted with the Ni3P/Ni3B/B−C/NF bifunctional electrocatalyst only required a voltage of 1.59 V at 50 mA cm−2 for water electrocatalysis under alkaline medium, and demonstrated long‐term stability for 48 h. This study provides a new technical path for the development of bifunctional of transition metal borides to promote the application of hydrogen production from water splitting.

Electroless plating of transition metal boride with high boron content as superior HER electrocatalyst

In Situ Construction of Ni Enriched Porous NiAl As Long-Lived Electrode for Hydrogen Evolution at High Current Densities

In situ analysis of a boron-based catalytic electrode with trace platinum for efficient hydrogen evolution in a wide pH range

Electroless Plating of Highly Efficient Bifunctional Boride‐Based Electrodes Toward Practical Overall Water Splitting

A superhydrophilic self-supported nickel/terbium oxide electrode for the alkaline hydrogen evolution reaction at high current density

Simultaneous Interfacial Chemistry and Inner Helmholtz Plane Regulation for Superior Alkaline Hydrogen Evolution

Surface Modification towards Integral Bulk Catalysts of Transition Metal Borides for Hydrogen Evolution Reaction

Boron-doping induced electron redistribution of carbon-coated nickel nanoparticles towards efficient alkaline hydrogen evolution

Impact of compositional tuning on Ni-B electrocatalyst for efficient hydrogen evolution

Boron-doped CoP/nitrogen-doped carbon drives enhanced alkaline hydrogen evolution

Bimetallic Nitride Ni3Mo3N Microrods with Abundant Catalytic Sites Used as Efficient Electrocatalysts for Hydrogen Evolution Reaction

Boride-Mediated Synthesis of Highly Active Cobalt-Based Electrocatalyst for Alkaline Hydrogen Evolution Reaction

Nanocrystalline transition metal tetraborides as efficient electrocatalysts for hydrogen evolution reaction at the large current density

Heterogeneous Ni‐Boride/Phosphide Anchored Amorphous B‐C Layer for Overall Water Electrocatalysis

Electronically Modulated Nickel Boron by CeOx Doping As a Highly Efficient Electrocatalyst Towards Overall Water Splitting.

Interstitial boron-doped Ni 4 Mo nanoarray catalyst boosts stable hydrogen evolution reaction

Efficient overall water splitting using nickel boride-based electrocatalysts

3D Transition Metal Boride Monolithic Electrode for Industrial Hectoampere-Level Current Anion Exchange Membrane Water Electrolysis

Metal boride better than Pt: HCP Pd2B as a superactive hydrogen evolution reaction catalyst

Interfacial electronic engineering of Ni3ZnC0.7/Ni heterostructure embedded in N-doped carbon nanotubes for efficient alkaline electrocatalytic hydrogen evolution

Interfacial electronic engineering of a Ni<sub>3</sub>ZnC<sub>0.7</sub>/Ni heterostructure embedded in N-doped carbon nanotubes for efficient alkaline electrocatalytic hydrogen evolution