Abstract:ABSTRACT:Objective To develop corrosion electrochemistry method with spatial resolution.Methods Pure Ni and Ni-P alloy coatings on copper substrates were fabricated by electrodeposition. Scanning Electron Microscopy (SEM) and XRD were applied to check surface morphology and crystal structure of the alloy coatings. Scanning Electrochemical Microscopy (SECM) research was applied to monitor the failure behavior of typical Ni and Ni-P coating in different concentration of NaCl solution. Combined with COMSOL Multiphysics simulation, 2D and 3D models were built to quantify activity point size and feedback mechanism.Results The low concentration of chloride ion had the activation effect for pure Ni coating, while higher chloride ion concentration promoted corrosion occurrence. Ni-P alloy coating maintained good stability in a short immersion time in low concentration of chloride in the solution. After 6 hours soaking, there were typical active points and corrosion products for low P alloy coating, while after 24 hours soaking for high P alloy coating. The corrosion type for low P alloy coating in 0.1 mol/L NaCl solution was localized corrosion and uniform corrosion in 0.3 mol/L NaCl solution. The simulation results of approaching curve showed that the electrochemical process of corrosion products for FcMeOH was completely inert and fresh Cu surface was electrochemical activity. 3D simulation results showed that active points of Ni-P coating failure process were close to 10 micron. Conclusion The failure process including the formation of active points, the generation and accumulation of corrosion production of Ni and Ni-P coating in NaCl solution is dependent on the positive and/or negative feedback effect of SECM map-ping. Chloride ion promotes occurrence of corrosion process, and its concentration has a strong effect on the corrosion type for Ni-P coating. COMSOL multiphysics simulation results indicate that the feedback effect is strongly dependent on the distance between the tip and the substrate, and the size of active point for Ni-P coating is micron level.

Correlation Between Corrosion Behaviour and Semiconductor Characteristics of Passive Film on Incoloy 825 in Ammonium Chloride Solution

Effect of Chloride on Semiconducting Properties of Passive Films Formed on Supermartensitic Stainless Steel in Nahco3 Solution

Effect of hydrogen on the pitting corrosion behavior of Incoloy 825

The semi-conductor property and corrosion resistance of passive film on electroplated Ni and Cu-Ni alloys

Systematic Insight into Chloride Concentration, Applied Potential and Time Effect on the Passive Film of Cu-Zn-Ni Ternary Alloy in Alkaline Solution

A Pre-Passive State Observed for the Passive Film Formed on Alloy 625 in a Hydrochloric Acid Solution

Passivation and Depassivation of HPB335 Carbon Steel in Simulated Concrete Pore Solution

Influence of Temperature, Chloride Ions and Chromium Element on the Electronic Property of Passive Film Formed on Carbon Steel in Bicarbonate/carbonate Buffer Solution

Electrochemical corrosion and passive behavior of a new high-nitrogen austenitic stainless steel in chloride environment

Semiconductive Tendency of the Passive Film Formed on Super Austenitic Stainless Steel SR-50A in Acidic or Alkaline Chloride Solutions

Sensitivity of Corrosion Behavior for Fe-Based Amorphous Coating to Temperature and Chloride Concentration

Passivity Breakdown on 436 Ferritic Stainless Steel in Solutions Containing Chloride

The Effect of Chloride Ion on Corrosion Behavior of Ni-P Alloy Coating Using SECM Experiment and COMSOL Simulation

Effects of Hydrogen on Semiconductivity of Passive Films and Corrosion Behavior of 310 Stainless Steel

Effect of Chloride Ion Concentration on the Corrosion Behavior of 304 Stainless Steel Used in the Electric Water Heater

EFFECT OF CHLORIDE ION ON CORROSION BEHAVIOR OF N80 STEEL IN CO2 SOLUTIONS

Corrosion behavior and electrochemical properties of carbon steel, commercial pure titanium, copper and copper–aluminum–nickel alloy in 3.5% sodium chloride containing sulfide ions

Corrosion and passive behavior of AlxCrFeNi3−x (x = 0.6, 0.8, 1.0) eutectic high entropy alloys in chloride environment

Failure analysis of anion synergy on pitting behavior of liner 316L in sour water system by electrochemical tests

Mixed potential model for passivity characters of hyper-duplex stainless steel 2707 in ammonium carbonate solution containing chloride

Study on Stress Corrosion Cracking Behavior of Incoloy825/X65 Bimetallic Composite Pipe Welded Joint in Wet Hydrogen Sulfide Environment