Benzoxazine Monomers and Polymers Based on 3,3′-Dichloro-4,4′-Diaminodiphenylmethane: Synthesis and Characterization
Viktoria V. Petrakova,Vyacheslav V. Kireev,Denis V. Onuchin,Igor A. Sarychev,Vyacheslav V. Shutov,Anastasia A. Kuzmich,Natalia V. Bornosuz,Mikhail V. Gorlov,Nikolay V. Pavlov,Alexey V. Shapagin,Ramil R. Khasbiullin,Igor S. Sirotin
DOI: https://doi.org/10.3390/polym13091421
IF: 5
2021-04-28
Polymers
Abstract:To reveal the effect of chlorine substituents in the ring of aromatic amine on the synthesis process of benzoxazine monomer and on its polymerization ability, as well as to develop a fire-resistant material, a previously unreported benzoxazine monomer based on 3,3′-dichloro-4,4′-diaminodiphenylmethane was obtained in toluene and mixture toluene/isopropanol. The resulting benzoxazine monomers were thermally cured for 2 h at 180 °C, 4 h at 200 °C, 2 h at 220 °C. A comparison between the rheological, thermal and fire-resistant properties of the benzoxazines based on 3,3′-dichloro-4,4′-diaminodiphenylmethane and, for reference, 4,4′-diaminodimethylmethane was made. The effect of the reaction medium on the structure of the oligomeric fraction and the overall yield of the main product were studied and the toluene/ethanol mixture was found to provide the best conditions; however, in contrast to most known diamine-based benzoxazines, synthesis in the pure toluene is also possible. The synthesized monomers can be used as thermo- and fire-resistant binders for polymer composite materials, as well as hardeners for epoxy resins. Chlorine-containing polybenzoxazines require more severe conditions for polymerization but have better fire resistance.
polymer science