Sulfonic-Group-Grafted Ti 3 C 2 T x MXene: A Silver Bullet to Settle the Instability of Polyaniline toward High-Performance Zn-Ion Batteries
Ying Liu,Ziwen Dai,Wang Zhang,Yue Jiang,Jian Peng,Dianlun Wu,Bin Chen,Wei Wei,Xian Chen,Zhenjie Liu,Zhigang Wang,Fei Han,Dahu Ding,Lei Wang,Lina Li,Yingguo Yang,Yang Huang
DOI: https://doi.org/10.1021/acsnano.1c02215
IF: 17.1
2021-04-29
ACS Nano
Abstract:Polyaniline (PANI) is a promising cathode material for Zn-ion batteries (ZIBs) due to its intrinsic conductivity and redox activity; however, the achievements of PANI in high-performance ZIBs are largely hindered by its instability during the repeated charge/discharge. Taking advantage of the high conductivity, flexibility, and grafting ability together, a surface-engineered Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub> MXene is designed as a silver bullet to fight against the deprotonation and swelling/shrinking issues occurring in the redox process of PANI, which are the origins of its instability. Specifically, the sulfonic-group-grafted Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>(S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>) continuously provides protons to improve the protonation degree of PANI and maintains the polymer backbone at a locally low pH, which effectively inhibits deprotonation and brings high redox activity along with good reversibility. Meanwhile, the conductive and flexible natures of S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub> assist the fast redox reaction of PANI and concurrently buffer its corresponding swelling/shrinking. Therefore, the S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>-enhanced PANI cathode simultaneously achieves a high discharge capacity of 262 mAh g<sup>–1</sup> at 0.5 A g<sup>–1</sup>, a superior rate capability of 160 mAh g<sup>–1</sup> at 15 A g<sup>–1</sup>, and a good cyclability over 5000 cycles with 100% coulombic efficiency. This work enlightens the development of versatile MXene <i>via</i> surface engineering for advanced batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c02215?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c02215</a>.Schematic illustration of synthesizing S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>; photographs of S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI cathode; XRD patterns of Ti<sub>3</sub>AlC<sub>2</sub>, 1-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, PANI, and charged/discharged S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI; SEM and AFM images of Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, and S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI; TEM image of Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>; N<sub>2</sub> adsorption–desorption isotherm of Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI; EDS mapping of S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI; XPS spectra of Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, cycled Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI, and cycled S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI; FTIR spectra of Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub> and PANI; Raman spectra of Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, PANI, and CNTs; electrochemical test results of PANI, S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>, CNTs, Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI, and S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI with a high loading; voltage curves of bare Zn and carbon-coated Zn symmetrical cells and their morphology changes before and after cycling; proposed reduction mechanism of PANI; and capacity retention of the quasi-solid-state ZIBs after the destructive tests. Table S1. Polymer-based and MXene-based cathode materials for ZIBs. Table S2. Calculation of SO<sub>4</sub><sup>2–</sup> dopant/–SO<sub>3</sub><sup>–</sup> dopant ratios in S-Ti<sub>3</sub>C<sub>2</sub>T<sub><i>x</i></sub>/PANI cathode at different states (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02215/suppl_file/nn1c02215_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology