Multifunctional Epoxy Composites with Highly Flame Retardant and Effective Electromagnetic Interference Shielding Performances

Wenwen Guo,Yuyu Zhao,Xin Wang,Wei Cai,Junling Wang,Lei Song,Yuan Hu

DOI: https://doi.org/10.1016/j.compositesb.2020.107990

2020-01-01

Abstract:Multifunctional epoxy composites with low flammability, high ablation resistance, superior electrical conductivity and outstanding electromagnetic interference (EMI) shielding performances are prepared by a two-step procedure. The first step involves pyrolysis of lignin-resorcinol-glyoxal pre-polymer into carbon foams, while the second step is infiltrating flame retardant epoxy resins (FREP) into the highly porous carbon foams. SEM images show that the three-dimensional network microstructure of carbon foams is integrally preserved during infiltration by the epoxy resins, which could serve as an effective pathway for electron transport. For the flame-retardant carbon foam/epoxy (FREP-CF) composite, a UL-94 V-0 classification is achieved. In the cone calorimeter measurement, the peak heat release rate and the total heat release of the FREP-CF composite are reduced by 64% and 37%, respectively, compared to those of the original epoxy resin. The FREP-CF composite can resist approximately 1000 degrees C flame for 10 min with the temperature on the back side lower than 200 degrees C, which is much better than the EP-CF composite. Additionally, a notable electrical conductivity of 216 S/m and a superior EMI shielding effectiveness of 33.5 dB are achieved for the FREP-CF composite. This multifunctional epoxy composite enables it a promising candidate for electronics, aerospace and transportation applications.