Abstract:Calcium (Ca) is in principle a very attractive metal anode for rechargeable batteries due to the large abundance of calcium in the Earth’s crust, its low electrochemical potential, and its low cost 1 . Until rather recently 2 , however, stable plating and stripping of Ca and hence rechargeability of Ca-batteries was deemed impossible, due to the stable phases formed at the electrolyte/electrode interface, completely blocking Ca 2+ transfer 3 .Since this pivotal breakthrough, Ca-batteries have attracted more interest, but they are still in their very infancy and new battery designs – such as using novel electrolyte concepts – are needed to achieve stable cycling of Ca metal anodes, and this preferably at room temperature. Here we report on the use of molten salt electrolytes, i.e. binary and multi-component systems of inorganic cations and anions, and more specifically on their physico-chemical and electrochemical properties as a function of composition with special emphasis on the compositional entropy. By using completely solvent-free electrolytes issues associated with organic electrolytes and solvents, such as the blocking of Ca 2+ transfer and electrolyte flammability 3 , are avoided. Furthermore, they should/do not induce any large polarization, as opposed to ionic liquid-based electrolytes 4 . In more detail, using the Ca(FSI) 2 salt in combination with the analogous Li-, Na-, and KFSI salts in equimolar compositions, all with melting temperatures (significantly) above 100 °C, we can create electrolytes melting at ca. 60-75 °C for the ternary systems, which is further reduced to ca. 55 °C for the quaternary system. These lowered melting temperatures are achieved by increased entropy of mixing, reducing the Gibbs free energy. This can for example be illustrated by Raman spectroscopy via comparing the spectra of “as cast” electrolytes with the spectra for the ones “aged” for one week (Figure 1). Here the FSI anion band at 772 cm -1 (ν s S-N-S) 5 shows that the electrolytes partially (re-)crystallize/micro-separate for the ternary systems, but stay more stable for the quaternary system, which we, at least partially, attribute to an entropy effect. Reference s M. E. Arroyo-De Dompablo, A. Ponrouch, P. Johansson, and M. R. Palacín, Chem . Rev. , 120 , 6331–6357 (2020). A. Ponrouch, C. Frontera, F. Bardé, and M. R. Palacín, Nat. Mater. , 15 , 169–172 (2016). D. Aurbach, R. Skaletsky, and Y. Gofer, J . Electrochem Soc. , 138 , 3536–3545 (1991). Q. Pang et al. , Nature , 608 , 704–711 (2022). K. Matsumoto, T. Oka, T. Nohira, and R. Hagiwara, Inorg . Chem . , 52 , 568–576 (2013). Figure 1

Electrolyte Solvation Manipulation Enables Unprecedented Room‐Temperature Calcium‐Metal Batteries

Cation Replacement Method Enables High-Performance Electrolytes for Multivalent Metal Batteries

Multi‐Ions Electrolyte Enabled High Performance Voltage Tailorable Room‐Temperature Ca‐Metal Batteries

Revealing the solid electrolyte interface on calcium metal anodes

Plating and Stripping Calcium in an Organic Electrolyte.

Toward a Reversible Calcium‐Sulfur Battery with a Lithium‐Ion Mediation Approach

Plating and Stripping Calcium at Room Temperature

Anode chemistry in calcium ion batteries: A review

Molten Salt Based High Entropy Electrolytes for Calcium Batteries

Deciphering and Modulating Energetics of Solvation Structure Enables Aggressive High-Voltage Chemistry of Li Metal Batteries

Stable Low-Temperature Lithium Metal Batteries with Dendrite-Free Ability Enabled by Electrolytes with Cooperative Li+-Solvation

Reversible Magnesium Metal Anode Enabled by Cooperative Solvation/Surface Engineering in Carbonate Electrolytes

Correlation between Electrolyte Chemistry and Solid Electrolyte Interphase for Reversible Ca Metal Anodes

Anionic Coordination Manipulation of Multilayer Solvation Structure Electrolyte for High‐Rate and Low‐Temperature Lithium Metal Battery

Ion-regulating Hybrid Electrolyte Interface for Long-life and Low N/P Ratio Lithium Metal Batteries

A Small Molecular Cathode for High‐Performance Calcium Metal Batteries

Electrolyte and interphase engineering through solvation structure regulation for stable lithium metal batteries

Electrolyte Solvation Engineering Stabilizing Anode‐Free Sodium Metal Battery With 4.0 V‐Class Layered Oxide Cathode

Strongly Solvating Triglyme-based Electrolyte Realizes Stable Lithium Metal Batteries at High-Voltage and High-Temperature

Aggregate-Dominated Dilute Electrolytes with Low-Temperature-Resistant Ion-Conducting Channels for Highly Reversible Na Plating/Stripping

Synchronous Regulation on Solvation Structure and Interface Engineering to Enable Reversible Magnesium Metal Batteries