A Comparative Study of Gas-phase Fluorination and Nano-Al2O3 Doping on Space Charge Behavior and Trap Level in Epoxy Resin
Zijia Shen,Feipeng Wang,Muhammad Zeeshan Khan,Zhengyong Huang,Li He,Yushuang He,Jian Li
DOI: https://doi.org/10.1109/tdei.2021.008950
IF: 2.509
2021-01-01
IEEE Transactions on Dielectrics and Electrical Insulation
Abstract:In this work, the effect of gas-phase fluorination concurrent with nano-Al2O3 doping on space charge distribution, as well as trap level and density of epoxy resin, is investigated. Epoxy resins with different concentrations of Al2O3 nano-fillers (0, 1, 3, and 5 wt%) are prepared and fluorinated by a gas mixture of F2/N2 (20/80 v/v) for 30 min at 40 °C and 0.05 MPa. Fourier-transform infrared (FTIR) spectroscopy confirms the breakage of molecular-chain during the gas-phase fluorination process. The space charge behavior is observed by the pulsed electroacoustic (PEA) method before and after fluorination. PEA results indicate that 30-minute fluorination is useful against space charge injection into the bulk of epoxy resin/Al2O3 nanocomposites. The trap density and trap energy level distribution are determined by isothermal surface potential decay (ISPD) measurement. The results indicate that fluorination introduces shallow traps on the surface, which can increase the conductivity of surface, and, thus, the trap depth is considerably reduced after fluorination. Moreover, it is found that incorporating 1 wt% nano-Al2O3 particles into epoxy resin can level up the energy level of deep traps. However, further increasing the nano-Al2O3 concentration, e.g., 3 and 5 wt%, promises the overlap of interaction zones between polymer matrix and nanoparticles, reducing the trap energy level.