Constructing An Interlaced Catalytic Surface Via Fluorine‐doped Bimetallic Oxides for Oxygen Electrode Processes in Li–O2 Batteries
Zongqiang Sun,Xiaodong Lin,Chutao Wang,Yanyan Tan,Wenjie Dou,Ajuan Hu,Jiaqing Cui,Jingmin Fan,Ruming Yuan,Mingsen Zheng,Quanfeng Dong
DOI: https://doi.org/10.1002/adma.202404319
IF: 29.4
2024-05-30
Advanced Materials
Abstract:Lithium–oxygen (Li–O2) batteries, renowned for their exceptionally high theoretical energy density, have garnered significant interest as a prime candidate for future electric device development. However, practical testing often yields unsatisfactory capacity due to the tendency of their solid‐phase discharge products to cover active sites on the electrode surface. Optimizing the growth mechanism of these solid‐phase products and addressing the storage issue to narrow the gap between actual and theoretical capacities stands as the core challenge in Li–O2 battery development. Here, a fluorine‐doped bimetallic cobalt‐nickel oxide (CoNiO2–xFx/CC) with an interlaced catalytic surface (ICS) and an open, corncob‐like structure is proposed as an oxygen electrode. Unlike conventional oxide electrodes with a "single adsorption catalytic mechanism", the ICS of the CoNiO2–xFx/CC electrode offers a compelling "competitive adsorption catalytic mechanism". This is attributed to the diverse selective sites within the ICS, where oxygen sites preferentially facilitate oxygen conversion due to their higher affinity for oxygen, while fluorine sites preferentially contribute to the growth of Li2O2 owing to their stronger affinity for LiO2. This transformation in the formation mechanism of Li2O2 and its morphology from film along the electrode surface to toroidal particles effectively mitigates the issue of buried active sites. Additionally, the unique structure of the CoNiO2–xFx/CC electrode aids in the storage and decomposition of Li2O2 products. Its corncob‐like open architecture not only promotes the capture and release of oxygen but also facilitates the formation of well‐contacted Li2O2/electrode interfaces, akin to a "corn on the cob" design. Consequently, the Li–O2 battery employing the CoNiO2–xFx/CC cathode demonstrates a high specific capacity of up to 30923 mAh g–1 and a lifespan exceeding 580 cycles, surpassing most reported metal oxide‐based cathodes. This work offers a promising solution to the issues of buried active sites and storage of insoluble products in metal‐air batteries. This article is protected by copyright. All rights reserved
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology