Abstract:Due to the well dispersibility of graphene oxide (GO) in aqueous solution, it is very difficult to separate GO after adsorption. Therefore, various organic/inorganic molecules have been composited with GO to produce novel adsorbents with relatively lower dispersibility and better adsorption performance. The rational selection of these organic/inorganic molecules seems very important. In this work, three-dimensional (3D) (graphene oxide-N-benzyloxycarbonylglycine) GO-ZG composites were synthesized by an easy-to-operate, one-step hydrothermal method. The 3D GO-ZG composites were illustrated by scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) spectroscopy, X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), high-resolution transmission electron microscopy (HR-TEM), powder x-ray diffraction (PXRD), Raman spectroscopy and specific surface area (SSA) analysis. The effects of GO-to-ZG mass ratio (x: y), hydrothermal reaction time, and hydrothermal reaction temperature were investigated. The adsorption properties of 3D GO-ZGx:y composites toward rare earth elements (REEs) were studied. The results showed that the composite with a GO-to-ZG mass ratio of 2:1, reaction time of 6 h, and reaction temperature of 120 ºC possessed the best adsorption performances. Further investigation of the adsorption conditions on 3D GO-ZG2:1/6 h/120 ℃ composites toward REEs including initial solution pH value, contact time, initial REE3+ concentration, and contact temperature was carried out. The adsorption of REEs could reach equilibrium in 60 min at room temperature. The adsorption capacities of 3D GO-ZG2:1/6 h/120 ℃ composite for La3+, Yb3+, Nd3+, Er3+ and Y3+ were 44.56, 53.64, 45.96, 50.48 and 30.63 mg·g-1, respectively. Ten adsorption/desorption cycles revealed that GO-ZG2:1/6 h/120 ℃ composite possessed good stability and recoverability. The adsorption mechanism of REEs by GO-ZG2:1/6 h/120 ℃ composite can be summarized as ion exchange, surface complexation, and electrostatic attraction. The as-prepared GO-ZG2:1/6 h/120 ℃ composite might be used as a renewable and structurally stable adsorbent in the adsorption.

Behavior and Mechanism of Graphene Oxide-Tris(4-aminophenyl)amine Composites in Adsorption of Rare Earth Elements

Scavenging mechanism of rare earth metal ions in water by graphene oxide

Impregnation synthesis of a novel macroporous silica-based TODGA polymeric composite and its application in the adsorption of rare earths in nitric acid solution containing diethylenetriaminepentaacetic acid

Preparation of A Novel Macroporous Silica-Based Diglycolamide Derivative-Impregnated Polymeric Composite and Its Adsorption Mechanism for Rare Earth Metal Ions

Three-dimensional hybrid nitrogen/oxygen-containing components modified graphene oxide as a recyclable adsorbent for rapid adsorption of REEs

Rational assembly of GO-based heterocyclic sulfur- and nitrogen-containing aerogels and their adsorption properties toward rare earth elementals

Preparation of a Novel Macroporous Silica-Based 2,6-Bis(5,6-diisobutyl-1,2,4-triazine-3-yl)pyridine Impregnated Polymeric Composite and Its Application in the Adsorption for Trivalent Rare Earths

Construction of a novel nitrogen- and oxygen-containing GO-based composite with specific adsorption selectivity

Rare Earth Ions Adsorption Onto Graphene Oxide Nanosheets

Engineering of 3D architectures with yttrium on reduced-graphene oxide nanosheets for effective co-adsorption of tetracycline and phosphate

Highly efficient enrichment and adsorption of rare earth ions (yttrium(III)) by recyclable magnetic nitrogen functionalized mesoporous expanded perlite

Recovery of Some Rare-Earth Elements by Sorption Technique onto Graphene Oxide

Interactions Between Th(iv) and Graphene Oxide: Experimental and Density Functional Theoretical Investigations

Selective adsorption and high recovery of La<SUP>3+</SUP> using graphene oxide/poly (<i>N</i>-isopropyl acrylamide-maleic acid) cryogel

Graphene oxide-Bicine composite as a novel adsorbent for removal of various contaminants from aqueous solutions

A Facile One-Pot Strategy to Functionalize Graphene Oxide with Poly(amino-phosphonic Acid) Derived from Wasted Acrylic Fibers for Effective Gd(III) Capture

Construction of Ion-Imprinted Graphene Oxide Mixed-Matrix Membranes for Selective Adsorption and Separation of Tm3

Understanding the Adsorption of Rare-Earth Elements in Oligo-Grafted Mesoporous Carbon

Preparation of 4-Amino-3-hydrazino-1,2,4-triazol-5-thiol-Modified Graphene Oxide and Its Greatly Enhanced Selective Adsorption of Gallium in Aqueous Solution

Mechanistic insights into the adsorption and extraction of rare earth ions using oxygen- and phosphorus-doped porous graphitic carbon nitride

Graphene Oxide Covalently Functionalized with 5-Methyl-1,3,4-thiadiazol-2-amine for pH-Sensitive Ga3+ Recovery in Aqueous Solutions