Phase Transition, Ferroelectric and Piezoelectric Properties of B-site Complex Cations (Fe0.5nb0.5)4+-Modified Ba0.70Ca0.30TiO3 Ceramics
Cai-Xia Li,Yue-Nan Hong,Bin Yang,Shan-Tao Zhang,Dan-Qing Liu,Xi-Ming Wang,Qian Liu,Lei Zhao,Wen-Wu Cao
DOI: https://doi.org/10.1016/j.ceramint.2019.12.214
IF: 5.532
2019-01-01
Ceramics International
Abstract:Ba0.70Ca0.30Ti1-x(Nb0.5Fe0.5)(x)O-3 lead-free ceramics (abbreviated as BCTNFx, x = 0-0.12) were prepared by solid-state reaction method. The influence of B-site (Fe0.5Nb0.5)(4+) substitution on phase structure, microstructure, dielectric, ferroelectric and piezoelectric properties of Ba0.70Ca0.30TiO3 ceramics were systematically studied. The BCTNFx ceramics consist of diphasic tetragonal (T) and orthorhombic (O) phases at x = 0-0.04, pseudocubic (PC) and O phases at x = 0.05-0.08, cubic (C) and O phases at 0.08 < x <= 0.12. Increase of (Fe0.5Nb0.5)(4+) doping improves sinterability, depresses the ferroelectric - paraelectric phase transition temperature (T-m) monotonically from 128 degrees C at x = 0 to -86 degrees C at x = 0.12, induces enhanced relaxor behavior and weakens piezoelectric properties. The room temperature relative dielectric constant (epsilon(r)) and dielectric loss tangent (tan delta) increase with increasing x and reach the maximum values of 4869 and 0.06 respectively at x = 0.06. Whereas the average grain size (abbreviated as AGS), ferroelectric properties and electric field induced strain increase significantly by introducing 2.0 mol% B-site complex cations (Fe0.5Nb0.5)(4+) into Ba0.70Ca0.30TiO3 ceramics. The BCTNF0.02 ceramics achieve optimal electrical properties with epsilon(r) = 1268, tan delta = 0.03, T-m = 102 degrees C, P max = 12.8 mu C/cm(2), P-r = 6.1 mu C/cm(2), E-c = 6.0 kV/cm, d(33) = 117 pC/N, k(p)% = 0.18%, Q(m) = 236, bipolar S-max% = 0.20%, unipolar S-max% = 0.16% and d(33)* = 314 pm/V. The variation of electrical properties of BCTNFx ceramics is attributed to the combined action of grain size effect, phase transition, weakness of octahedral distortion, clamping effects of the internal bias electric field E-i on domain wall motion induced by B-site cations(Fe0.5Nb0.5)(4+) displacement.