Abstract:Preparation under non-identical conditions involving the reduction of sol–gel-derived precursors of various Zn:Fe atomic ratios (0.97:0.03, 0.8:0.2 and 0.4:0.6) in a hydrogen-containing atmosphere was used to obtain composites of nanosized ferromagnetic (FM) α-Fe and antiferromagnetic (AFM) FeO in different concentrations and of the desired magnetic responses. ZnO nanoparticles, developed in all preparation stages, served primarily as a matrix for the separation of Fe (and FeO) nanoparticles, preventing their agglomeration and coarsening. The average crystallite/particle size is about 5–32 nm, 10–75 nm and 21–31 nm for FeO, Fe and ZnO, respectively. Magnetisation investigations of FeO-Fe-ZnO nanocomposites revealed a coexistence of ferromagnetic and superparamagnetic behaviours ascribed to the Fe nanoparticles in different magnetic states. All samples exhibit the exchange bias effect, EB. Values up to 375 Oe for coercivity at 300 K, 600 Oe for coercivity, 223 for coercivity enhancement and 243 Oe for EB field at 5 K were measured. The magnitude of EB depends on the processing conditions – the EB field and coercivity enhancement are larger for samples processed under conditions of a higher degree of non-equilibrium. The presence of FeO appears crucial for the occurrence of EB, irrespective of its quantity. The EB is ascribed primarily to the exchange coupling between the AFM and FM spins at the FeO/Fe interfaces of nanostructures after field-cooling from above the T N of FeO and below the Curie temperature of Fe. An approach based on magnetically disordered AFM/FM interfaces featuring like spin-glass systems was adopted to explain the EB effects. An aspect of practical relevance is the suppression of room temperature coercivity in apparent correlation with the training of the EB; an attempt has been made to understand the origin of this suppression.

Exchange-biased Nanocomposite Ferromagnetic Insulator

Robust Ferromagnetic Insulating and Large Exchange Bias in LaMnO3:CoO Composite Thin Films

Exchange Bias Effect and Magnetic Properties in ${\Hbox{la}}_{0.7}{\hbox{sr}}_{0.3}{\hbox{mno}}_{3}\hbox{-}{\Hbox{nio}}$ Nanocomposite Films

Tuning The Competition Between Ferromagnetism And Antiferromagnetism In A Half-Doped Manganite Through Magnetoelectric Coupling

Double-Exchange Bias Modulation under Horizontal and Perpendicular Field Directions by 3D Nanocomposite Design

Exchange Bias in a La 0.67 Sr 0.33 MnO 3 /NiO Heterointerface Integrated on a Flexible Mica Substrate

Exchange Bias Effect in LaFeO3: La0.7Ca0.3MnO3 Composite Thin Films

Interfacial Ferromagnetic Coupling and Positive Spontaneous Exchange Bias in SrFeO3- x/La0.7Sr0.3MnO3 Bilayers

Realization of exchange bias control with manipulation of interfacial frustration in magnetic complex oxide heterostructures

Exchange Bias Effects in Ferromagnetic MnSb2Te4 Down to a Monolayer

Exchange Bias in LiNi0.5Mn1.5O4–NiO Nanocomposites

Exchange Bias Effects in Ferromagnetic MnSb 2 Te 4 down to a Monolayer

Interface-Induced Enhancement of Ferromagnetism in Insulating LaMnO3 Ultrathin Films

Exchange Bias Effects in Ferromagnetic MnSb<sub>2</sub>Te<sub>4</sub> down to a Monolayer

Magnetic behaviors of exchange-biased Fe(FM)-FeO(AFM)-ZnO nanocomposites of different iron concentrations prepared under non-identical conditions with annealing in a reducing atmosphere

Microstructural Underpinnings of Giant Intrinsic Exchange Bias in Epitaxial NiCo2O4 Thin Films

Exchange bias in Sm$ _{2} $NiMnO$ _{6}$/BaTiO$ _{3}$ ferromagnetic-diamagnetic heterostructure thin films

Giant spontaneous exchange bias in an antiperovskite structure driven by a canted triangular magnetic structure

Efficient energy and memory storage capabilities in optimized BiFeO3/MnMoO4/NiFe2O4 triphasic composites for futuristic multistate devices

Magnetic Structures at the Ferromagnetic NiFe and Antiferromagnetic NiMn Interface in Exchange-Biased Films: Role of Noncollinear Magnetism and Roughness

Nitrogen-Based Magneto-ionic Manipulation of Exchange Bias in CoFe/MnN Heterostructures