Abstract:A novel charring foaming agent N-methyl triazine-ethylenediamine copolymer defined as MTEC was synthesized from cyanuric chloride, methylamine and ethylenediamine through nucleophilic reaction. Its chemical structure was well characterized by Fourier transform infrared spectroscopy, elemental analysis and C-13 solid-state nuclear magnetic resonance. The wettability of flame retardant was evaluated by water contact angle (CA) tests, and the synthesized MTEC present excellent hydrophobic property with the water CA of 117 degrees. Meanwhile, the water CA of the prepared intumescent flame retardant (IFR) system containing MTEC, ammonium polyphosphate and silica reached 104 and also presented hydrophobic property. The obtained IFR was incorporated into polypropylene (PP) resin to prepare flame retardant PP composites, and the flame retardancy, thermal degradation behavior, water resistance and flammability behavior for IFR-PP were investigated by limiting oxygen index (LOI), vertical burning test (UL-94), cone calorimeter and thermogravimetric analysis (TGA) tests. Water resistant properties of IFR-PP composites were evaluated by soaking the samples into distilled water at 70 degrees C for 168 h. The results demonstrated that IFR-PP samples both passed UL-94 V-0 flammability rating before water treated and after hot water soaking and drying when the loading amount of IFR was 22 wt %, the LOI value of IFR-PP only decreased from 29.6 to 293% and the mass loss percent was only 0.17 and 0.69% for 3.2 and 1.6 mm samples after water soaking and drying. The TGA results indicated that the incorporation of IFR promoted PP matrix decomposition and charring at a relative low temperature, and then enhanced the char yield and thermal stability for IFR-PP composites at high temperature. The cone calorimeter tests revealed that the introduction of IFR greatly decreased the combustion parameters, such as heat release rate (HRR), smoke production rate (SPR) and so on. After water resistance test, the combustion parameter for IFR-PP was slightly increased. The scanning electron microscopy (SEM) tests indicated the introduction of IFR benefited to the formation of a sufficient, intumescent and homogeneous char layer on the materials surface during burning, which effectively prevented the underlying materials from further degradation and combustion. The structure and morphology of char layer for IFR-PP remained very well after water treated, consequently the water-treated IFR-PP presented excellent flame retardancy. (C) 2016 Elsevier Ltd. All rights reserved.

Flame Retardant Efficiency of Modified Para-Aramid Fiber Synergizing with Ammonium Polyphosphate on PP/EPDM

Hyperbranched Polyamide-Amine Based Phosphorous-Containing Flame Retardant for Simultaneous Flame Retardancy and High Performance of Polypropylene

Synthesis and Flame Retardant Behavior of Phosphorous- and Nitrogen-Containing Copolymer and Its Application in Polypropylene

High-efficiency ammonium polyphosphate intumescent encapsulated polypropylene flame retardant

Effects of 1-Aminoethylidenediphosphonic Acid and Its Synergistic Composition on Flame Resistance of Polypropylene

Flame retardant effect of cytosine pyrophosphate and pentaerythritol on polypropylene

Ammonium Polyphosphate and Silicon-Containing Cyclotriphosphazene: Synergistic Effect in Flame-Retarded Polypropylene

Synergistic effect between a char forming agent (CFA) and microencapsulated ammonium polyphosphate on the thermal and flame retardant properties of polypropylene

Hyperbranched Phosphorus/nitrogen-Containing Polymer in Combination with Ammonium Polyphosphate As a Novel Flame Retardant System for Polypropylene

Effect of Novel Copolyamide Charring Agents on Flame‐retarded Polypropylene

Component Ratio Effects Of Hyperbranched Triazine Compound And Ammonium Polyphosphate In Flame-Retardant Polypropylene Composites

Influence of Melamine Polyphosphate and Cage-Like Pentaerythritol Phosphate Synergistic Flame Retardant on Polypropylene/rice Husk Composite

Synergistic effect of expandable graphite and intumescent flame retardants on the flame retardancy and thermal stability of polypropylene

Synthesis of N-Methyl Triazine-Ethylenediamine Copolymer Charring Foaming Agent and Its Enhancement on Flame Retardancy and Water Resistance for Polypropylene Composites

Synergistic Effect of Aryl Phosphate on Intumescent Flame Retardant Polypropylene

An Efficient and Convenient Strategy Toward Fire Safety and Water Resistance of Polypropylene Composites Through Design and Synthesis of a Novel Mono‐component Intumescent Flame Retardant

Synergistic Effect of Zeolite and Hindered Amine Containing Substances on Intumescent Flame Retardant Polypropylene

Study on PP Flame Retarded with Aryl Phosphate and Intumescent Flame Retardant Compound

Flame-retardant Effects of NH2-MIL-53(Al) in Combination with Phosphorus-Containing and Nitrogen-Containing Flame Retardants on Polypropylene

Flame-Retardant and Thermal Degradation Mechanism of Caged Phosphate Charring Agent with Melamine Pyrophosphate for Polypropylene

Flame Retardant Mechanism of an Efficient Flame-Retardant Polymeric Synergist with Ammonium Polyphosphate for Polypropylene