Numerical Study on Fatigue Behavior and Strengthening of Steel Pipes with a Surface Crack
Gang Wang,Zhuxuan Li,Tao Chen,Peichen Peng,Zhigang Xiao
DOI: https://doi.org/10.1016/j.tafmec.2023.104003
IF: 4.374
2023-01-01
Theoretical and Applied Fracture Mechanics
Abstract:Recently, metallic pipes have been extensively utilized in civil and marine engineering, whereas surface cracks are quintessential flaws of steel pipes, the emergence of which may trigger fatigue failure. The work of this paper is mainly a numerical study on the fatigue behavior and strengthening of steel pipes with a part-through circumferential crack under four-point bending. A crack propagation model was proposed, and the corre-sponding surface crack growth simulation was subsequently implemented through finite element method (FEM) in conjunction with Python scripting. The numerical models, including unrepaired and carbon fiber reinforced polymer (CFRP)-repaired pipes, were further validated by evaluating the fatigue life and stress intensity factor (SIF). Based on the verified models, case studies were conducted, and two parameters, which are initial crack sizes and CFRP layer number, were quantitatively analyzed to assess their influence on SIFs along the crack tip, surface crack propagation, and the development of crack aspect ratio. The results reveal that initial crack sizes have an impact on the fatigue behavior of steel pipe to varying extents, especially on the SIF, crack propagation rate, and tendency of crack aspect ratio development, however, the final crack aspect ratio is largely unaffected. Moreover, reinforcing with CFRP can substantially reduce the SIF, enlarge the crack aspect ratio, and reduce the crack propagation rate, thereby dramatically extending the fatigue life. This study can serve as a reference for future research or design regarding the fatigue of steel pipe.