Design and Synthesis of Phenyl Silicone Rubber with Functional Epoxy Groups Through Anionic Copolymerization and Subsequent Epoxidation

Yimin Wang,Renwei Cao,Meihao Wang,Xiaomin Liu,Xiuying Zhao,Yonglai Lu,Anchao Feng,Liqun Zhang

DOI: https://doi.org/10.1016/j.polymer.2019.122077

IF: 4.6

2020-01-01

Polymer

Abstract:In this paper, we have developed epoxidized phenyl silicone rubber (EMVPQ) with good oil and radiation resistance by anionic ring-opening copolymerization and further epoxidation modification. Silicone rubbers with both phenyl and epoxy groups were firstly synthesized and main properties of the material were characterized. When the phenyl content in EMVPQ was increased from 5% to 20%, the damping loss peak shifted to the high temperature by 36 degrees C and the effective damping temperature range was widened by 3 degrees C. The tensile strength of EMVPQ with 20% phenyl content did not change before and after irradiation. When the epoxy content is only 13%, the EMVPQ retained mechanical properties after immersion at 25 degrees C or 100 degrees C for 72 h, but a commercial sample substantially lost its mechanical properties. This work not only promotes the research of epoxidized phenyl silicone rubber, but also opens an effective way for the preparation of high-performance aerospace materials.