Abstract:The MgAl layered hydrotalcites (MgAl-LDHs) precursors with submicron-scale were synthesized by introducing ethanol into hydrothermal synthesis method. The synthesis process parameters were optimized by orthogonal experiment, and then the composite metal oxide (MgAlOx) was obtained after the calcination process. The crystal phase, morphology and alkalinity of both hydrotalcite precursors and solid base oxides were characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and the temperature-programmed desorption of CO2(CO2-TPD), respecitively. Finally, the catalytic performance of MgAlOx was evaluated by the depolymerization test of calcium lignosulfonate. The products including solid, liquid, gas three phases, were analyzed by gel permeation chromatography (GPC), gas chromatography/mass spectrometry (GC-MS) and gas chromatography (GC). The results indicated that 140-230 nm of MgAl-LDHs were regulated by adding 15% (volume fraction) C2H5OH to the hydrothermal system, the optimal synthesis condition considered from relative crystallinity was n(Mg)/n(Al)=3, pH=12 and the temperature of 80 degrees C for 24 h. the MgAlOx obtained after the calcination of MgAl-LDHs at 600 degrees C for 6 h under air atmosphere. The optimal depolymerization of calcium lignosulfonate was 270 degrees C, 4 h, the addition of 65% (volume fraction) C2H5OH and m(MgAlOx)/m(CLS)=1/2. The gas-liquid-solid three-phase yield distribution was 4.50%, 58.30% and 37.20% under the above condition, the liquid yields increased by 13.30% with the addition of MgAlOx, the main components of liquid products were phenolics, aromatics, esters and others. Moreover, the selectivity of oxy-containing compounds was 79.05% (phenolics of 66.06%, esters of 12.99%). Fortunately, MgAlOx would also keep high reactivity and stability even after four cycles of reactions.

Catalytic depolymerization of calcium lignosulfonate to high-value oxygenated aromatic compounds over the efficient Fe 2 O 3 -La 0.8 Sr 0.2 FeO 3

Catalytic Depolymerization of calcium lignosulfonate by NiMgFeOx derived from sub-micron sized NiMgFe Hydrotalcite prepared by introducing hydroxyl compounds

Production of Oxygen-containing Compounds Catalytic from Depolymerization of Calcium Lignosulphonate by Submicron-scale MgAl Solid Base

Depolymerization of Lignosulfonate Catalyzed by Different Solid Base Oxides to Prepare Phenolic Compounds

Ni modulates the coordination environment of cations in Fe 3 O 4 to efficiently catalyze lignin depolymerization

Efficient conversion of Kraft lignin to guaiacol and 4-alkyl guaiacols over Fe-Fe3C/C based catalyst under supercritical ethanol

Efficient Lignin Depolymerization Process for Phenolic Products with Lignin-Based Catalysts and Mixed Solvents

One-step valorization of calcium lignosulfonate to produce phenolics with the addition of solid base oxides in the hydrothermal reaction system

Efficient and stable Fe-Ce-Al catalyst for catalytic deoxygenation of lignin for phenol and hydrocarbon-rich fuel: Effect of the synthesis method

Electrocatalytic Lignin Valorization into Aromatic Products via Oxidative Cleavage of Cα−Cβ Bonds

Aromatic chemicals by iron-catalyzed hydrotreatment of lignin pyrolysis vapor

Depolymerization of Lignin by Catalytic Oxidation with Aqueous Polyoxometalates

Selective catalytic conversion of Kraft lignin into monoaromatic hydrocarbons over niobium oxide catalysts

Catalytic Oxidation of Lignin in Solvent Systems for Production of Renewable Chemicals: A Review

Catalytic transfer hydrodeoxygenation of guaiacol to phenol with formic acid over N-doped carbon encapsulated non-noble alloy catalysts

Enhancing aromatic hydrocarbon formation via catalytic depolymerization of lignin waste over Ru/WOx/N-C catalyst

Electro-oxidative Depolymerization of Lignin for Production of Value-Added Chemicals

Catalytic Hydrodeoxygenation of Guaiacol to Cyclohexanol over Bimetallic NiMo-MOF-Derived Catalysts

Breaking the lignin conversion bottleneck for multiple products: Co-production of aryl monomers and carbon nanospheres using one-step catalyst-free depolymerization

Oxidative Depolymerisation of Lignosulphonate Lignin into Low-Molecular-Weight Products with Cu–Mn/δ-Al2O3

Selective catalytic depolymerization of lignin to guaiacols over Mo-Mn/sepiolite in supercritical ethanol