Anisotropic Thermal Conductivity and Associated Heat Transport Mechanism in Roll-to-roll Graphene Reinforced Copper Matrix Composites
K. M. Yang,Y. C. Ma,Z. Y. Zhang,J. Zhu,Z. B. Sun,J. S. Chen,H. H. Zhao,J. Song,Q. Li,N. Q. Chen,H. Y. Ma,J. Zhou,Y. Liu,T. X. Fan
DOI: https://doi.org/10.1016/j.actamat.2020.07.021
IF: 9.4
2020-01-01
Acta Materialia
Abstract:Owing to the high strength of copper (Cu) and high in-plane thermal conductivity (K-T) of graphene (Gr), Gr/Cu composites are increasingly demanded as the advanced thermal management materials to ensure the heat dissipation. The heat transport performance is primarily influenced by two aspects: (1) Intrinsic parameters of Gr, including its crystallinity, layer number (N), coverage and spatial distribution and (2) Gr/Cu interface related properties, such as interface bonding, residual strain and defects near the interface. In this work, by combining roll-to-roll (R2R) chemical vapor deposition (CVD) and subsequent hot isostatic pressing (HIP) techniques, highly paralleled Gr reinforced Cu matrix composites with controllable N were fabricated. Experimental results show that similar to 5-6L Gr/Cu composites manifest the highest degree of anisotropy, including (1) the highest K-r (394 +/- 5 W/mK, similar to 22% higher than pure Cu counterpart), and (2) the lowest through-plane thermal conductivity (K-z) (257 +/- 4 W/mK, similar to 25% lower than pure Cu counterpart). When N varies from 1 to 5, the continuously increased K-r and decreased K-z are majority influenced by intrinsic properties of Gr, which is also validated by multiscale simulations and time-domain thermoreflectance analysis. When N increases to similar to 10, both K-r and K-z exhibit opposite trend, that may attribute to the reduced Gr coverage and large volume fraction of amorphous carbon. Moreover, the residual strain and defects at the interface could lower both K-r and K-z as well. This study suggests that advanced synthesis of high-crystallinity thick Gr may be promising to obtain superb K-r in Cu matrix composites. (c) 2020 Published by Elsevier Ltd on behalf of Acta Materialia Inc.