Abstract:Ordered Pt alloy electrocatalysts supported on carbon nanomaterials have attracted widespread attention, especially for the oxygen reduction reaction (ORR), due to the catalytic performance derived from their unique electronic and geometric structures. However, it is still urgent to fabricate uniform and structurally ordered Pt alloy electrocatalysts based on simple methods. Herein, a two-step direct annealing method was applied to synthesize uniform and ordered PtFe alloy nanoparticles loaded on single-wall carbon nanohorns (SWCNHs) under the protection of a thin N-doped carbon (NC) shell, which was in situ generated from the polymerization and pyrolysis of a small organic ligand, namely, aniline, during the first annealing treatment. After the second annealing treatment in a H2 atmosphere for 9 h, the obtained sample, denoted as /SWCNHs(H2-9h), exhibited uniform and ordered PtFe nanoparticles with a face-centered tetragonal (fct) structure (ordered degree: >80%, mean size: ∼5.2 nm) on the graphitic SWCNH support. Without removing the NC shell, the /SWCNHs(H2-9h) sample showed mass activity (1.53 A/mgPt at 0.9 V) and specific activity (3.61 mA/cm2 at 0.9 V) toward the ORR due to the enhanced electronic interaction derived from the ordered fct-PtFe structure. Importantly, it still retained high catalytic activity after a long-term stability test, mainly owing to the ordered fct-PtFe structure and the protection of the NC shell, which provides strong resistance toward the Fe leaching and nanoparticle aggregation, respectively. The presented strategy is generalized to fabricate different ordered PtM or Pt3M (M = Fe/Co) alloy electrocatalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.1c02434?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.1c02434</a>.Additional experimental results including the structure and composition characterizations and electrochemical testing results (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.1c02434/suppl_file/cs1c02434_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Simple synthesis of ordered platinum-gold nanoparticles with the enhanced catalytic activity for oxygen reduction reaction

Local Coordination and Ordering Engineering to Design Efficient Core-Shell Oxygen Reduction Catalysts

Multimetallic AuPd@Pd@Pt Core-Interlayer-shell Icosahedral Electrocatalysts for Highly Efficient Oxygen Reduction Reaction

Trimetallic Au@PtPd Mesoporous Nanorods As Efficient Electrocatalysts for the Oxygen Reduction Reaction

Catalytic Pt-on-Au Nanostructures: Why Pt Becomes More Active on Smaller Au Particles.

Synthesis of Self-Assembled PtPdAg Nanostructures with a High Catalytic Activity for Oxygen Reduction Reactions.

Facile Synthesis of Structurally Ordered Low-Pt-loading Pd–Pt–Fe Nanoalloys with Enhanced Electrocatalytic Performance for Oxygen Reduction Reaction

Twin-Directed Deposition of Pt on Pd Icosahedral Nanocrystals for Catalysts with Enhanced Activity and Durability toward Oxygen Reduction

The Catalytic Performance and Characterization of Nanoporous Gold Loading Platinum and Antimony (Oxidized) Catalysts Towards Cathode Oxygen Reduction Reaction

Composition-driven Shape Evolution to Cu-rich PtCu Octahedral Alloy Nanocrystals As Superior Bifunctional Catalysts for Methanol Oxidation and Oxygen Reduction Reaction

Native ligand carbonization renders common platinum nanoparticles highly durable for electrocatalytic oxygen reduction: annealing temperature matters

Synthesis of Structurally Stable and Highly Active PtCo3 Ordered Nanoparticles Through an Easily Operated Strategy for Enhanced Oxygen Reduction Reaction

One-pot facile synthesis of PtCu coated nanoporous gold with unique catalytic activity toward the oxygen reduction reaction

A novel core-shell nanostructure of Ti-Au nanocrystal with PtNi alloy skin: Enhancing the durability for oxygen reduction reaction

Direct epitaxial growth of Au nanoparticles on Pd metallene enables robust oxygen reduction electrocatalysis

Local tetragonal distortion of Pt alloy catalysts for enhanced oxygen reduction reaction efficiency

Pd9Au1@Pt/C core-shell catalyst prepared via Pd9Au1-catalyzed coating for enhanced oxygen reduction

Controlled Synthesis of High Metal-Loading, Pt-based Electrocatalysts with Enhanced Activity and Durability Toward Oxygen Reduction Reaction

Advances in Liquid-Phase Synthesis: Monitoring of Kinetics for Platinum Nanoparticles Formation, and Pt/C Electrocatalysts with Monodispersive Nanoparticles for Oxygen Reduction

Direct Thermal Annealing Synthesis of Ordered Pt Alloy Nanoparticles Coated with a Thin N-Doped Carbon Shell for the Oxygen Reduction Reaction

Precise control of platinum coordination environment on fullerene-derived catalysts for oxygen reduction reaction