Hydrothermal Liquefaction of Microalgae Using Fe3O4 Nanostructures As Efficient Catalyst for the Production of Bio-Oil: Optimization of Reaction Parameters by Response Surface Methodology

Sabariswaran Kandasamy,Bo Zhang,Zhixia He,Haitao Chen,Huan Feng,Qian Wang,Bin Wang,Narayanamoorthy Bhuvanendran,Sivakumar Esakkimuthu,Veeramuthu Ashokkumar,M. Krishnamoorthi

DOI: https://doi.org/10.1016/j.biombioe.2019.105417

2019-01-01

Abstract:The aim of the present work was focused on optimizing the hydrothermal liquefaction (HTL) of Spirulina platensis catalyzed by Fe3O4 nanostructures to enhance the bio-oil yield and quality of bio-oil using response surface methodology (RSM). The structural morphology and crystalline nature of the synthesized catalyst was determined using a scanning electron microscope (SEM), high resolution transmission electron microscopy (HR-TEM) and X-ray powder diffraction (XRD). Three of the vital reaction parameters such as temperature, holding time and catalyst dosage were optimized through central composite design. A maximum bio-oil yield of 32.33% was observed for the high temperature at 320 degrees C, 0.75 g of catalyst dosage and 37 min of resident time. The maximum conversion was found at a lower temperature of 272 degrees C, the bio-oil yield of 27.66% was obtained with 0.45 g of catalyst dosage and 24 min of holding time which is an energy efficient optimum condition. The maximum bio-oil yield was influenced at a lower temperature due to the high catalytic activity. While compared to higher temperatures were not much influence was observed. It clearly states that the catalyst dosage playing a critical role in the lower temperature HTL reaction. GC-MS and FT-IR analysis of the produced bio-oil exhibits significant characteristics for biofuel applications. The Fe3O4 catalyst was recyclable for up to eight repeated cycles and constant bio-oil yield for the last four cycles. It shows the excellent reproduction ability towards HTL of Spirulina sp.