Temperature Rise Characteristics of Coal-Koh Adduct under Microwave Heating and the Properties of Resultant Activated Carbon for Catalytic Methane Decomposition

Taiping Chen,Huanpeng Liu,Rushan Bie
DOI: https://doi.org/10.1016/j.jaap.2019.104739
IF: 6
2020-01-01
Journal of Analytical and Applied Pyrolysis
Abstract:Temperature rise characteristics of subbituminous coal impregnated with KOH in a wide range of KOH/coal ratio (w/w, 0.25 similar to 2) under microwave (MW) heating were investigated and the catalytic performance in methane decomposition (CMD) over the resultant activated carbon (AC) was measured. The results showed that with the increase of KOH content, the temperature rise ability of the coal-KOH adduct under MW-field increases gradually, and the maximum temperature that can be increased from 170 degrees C to 880 degrees C. The increase of aromaticity due to the structural rearrangement of the coal aromatic layers during KOH impregnation and the release of volatiles during MW-heating provides the main driving force for the continuous increase of temperature. When KOH/coal ratio is 1.5, it took 224 s for coal-KOH adduct to rise from room temperature to 800 degrees C, with the development of specific surface area (S-BET) and pore volume to the maximum of 661.8 m(2)/g and 0.512 cm(3)/g, respectively. However, the catalytic activity of AC with the largest S-BET for CMD is not the highest. At 800 degrees C and higher temperatures, the increase of active site number on the surface by the potassium intercalation mechanism promotes the catalytic activity of AC. Therefore, the research core of carbon-based catalysts from coal is to increase the number of active site, not the S-BET alone.
What problem does this paper attempt to address?