Abstract:The selective catalytic reduction (SCR) technique that converts NOx from the outlet of industrial boilers at low temperature (<200 degrees C) requires catalysts that possess both the oxidization property of NOx and the adsorption ability to NH3. However, owing to unsuitable redox capacity, most NH3-SCR catalysts such as MnO2/TiO2 and MnO2-CeO2/TiO2 suffer from poor activity and N-2 selectivity and SO2 poisoning. Benefiting from constructing mesoporous MnCeSmTiOx amorphous mixed oxides by the coprecipitation method, enhanced SO2-tolerant low-temperature NH3-SCR performance was achieved. The MnCeSmTiOx catalysts have an amorphous and mesoporous structure with a BET surface area of 214 m(2) .g(-1). The NO conversion could reach nearly 100% at 140-320 degrees C and maintain >90% at 400 degrees C and a gas hourly space velocity of 80,000h(-1). The selectivity of N-2 could be maintained at approximate to 100% at 100-320 degrees C and stay at >90% up to 400 degrees C. Besides, the MnCeSmTiOx catalyst preserves higher catalytic performance after introducing H2O and SO2 compared with the catalysts without adding Sm. The redox properties, acidic properties, and reaction intermediates of catalysts were analyzed by X-ray photoelectron spectroscopy, hydrogen temperature-programmed reduction, ammonia temperature-programmed desorption, oxygen temperature-programmed desorption, pyridine-IR, thermogravimetry-differential scanning calorimetry, and diffuse reflectance infrared Fourier transform. The synergistic effect of the Lewis acid sites and oxidation catalytic sites of mixed oxides serves for the conversion of NO to N-2 by following the Langmuir-Hinshelwood mechanism. Doping Sm into MnCeSmTiOx can increase oxygen vacancies and transfer electrons to Mn4+ and Ce4+, which facilities the formation of active adsorbed NO2, bidentate nitrate, and bridging nitrate intermediates and suppresses SO2 poisoning by inhibiting the oxidation of SO2 by Mn4+ and Ce4+. Our work could be beneficial to modulate the redox capacity of active sites on NH3-SCR catalysts so that NOx can be eliminated in complex flue gas at low temperatures.

Pr-doped Modified Fe–Mn/TiO2 Catalysts with a High Activity and SO2 Tolerance for NH3-SCR at Low-Temperature

An investigation on the promoting effect of Pr modification on SO2 resistance over MnOx catalysts for selective reduction of NO with NH3

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

The promotion effect of Pr doping on the catalytic performance of MnCeOx catalysts for low-temperature NH3-SCR

Fe and Mn mixed oxide catalysts supported on Sn-modified TiO 2 for the selective catalytic reduction of NO with NH 3 at low temperature

Improvement of Activity and SO2 Tolerance of Sn-Modified MnOx–CeO2 Catalysts for NH3-SCR at Low Temperatures

SO2 Promoted V2O5-MoO3/TiO2 Catalyst for NH3-SCR of NOx at Low Temperatures

Excellent sulfur tolerance performance over Fe-SO4/TiO2 catalysts for NH3-SCR: Influence of sulfation and Fe-based sulfates

Titania-Samarium-Manganese Composite Oxide for the Low-Temperature Selective Catalytic Reduction of NO with NH3

Improvement of sulfur and water resistance with Fe-modified S-MnCoCe/Ti/Si catalyst for low-temperature selective catalytic reduction of NO with NH3

Synthesis of CrOx/C Catalysts for Low Temperature NH3-SCR with Enhanced Regeneration Ability in the Presence of SO2

Converting Poisonous Sulfate Species to an Active Promoter on TiO2 Predecorated MnOx Catalysts for the NH3-SCR Reaction

Highly efficient NH3-SCR of NO over MnFeW/Ti catalyst at low temperature: SO2 tolerance and reaction mechanism

Design of robust Co-doped Mn3O4 spinel catalysts for selective catalytic reduction of NO with NH3 at low temperatures

In situ construction of heteroatom F-doped Mn3O4 spinel catalysts with robust activity and SO2 resistance for NH3-SCR at low temperature

SO2Poisoning Behaviors of Ca-Mn/TiO2Catalysts for Selective Catalytic Reduction of NO with NH3at Low Temperature

SO2 Resisting Pd-doped Pr1-x Cex MnO3 Perovskites for Efficient Denitration at Low Temperature

Improved Activity And So2 Resistance By Sm-Modulated Redox Of Mncesmtiox Mesoporous Amorphous Oxides For Low-Temperature Nh3-Scr Of No

Low-temperature selective catalytic reduction of NO on MnOx/TiO2 prepared by different methods

Facile Preparation of High-Performance Fe-doped Ce–Mn/TiO2 Catalysts for the Low-Temperature Selective Catalytic Reduction of NOx with NH3

Novel Synthesis of Reed Flower-Like SmMnOx Catalyst with Enhanced Low-Temperature Activity and SO2 Resistance for NH3-SCR.