Discovering Pd-B/C As a Potential Bifunctional Catalyst in the Formic Acid ↔ Carbon Dioxide Conversion Cycle
Bei Jiang,Kun Jiang,Wen-Bin Cai
DOI: https://doi.org/10.1149/ma2016-02/46/3418
2016-01-01
ECS Meeting Abstracts
Abstract:It is well known that facile interconversion of HCOOH and CO2 is very important in hydrogen production, direct formic acid fuel cell, as well as neutral emission of CO2. In the past few years, we have investigated chemical and electrochemical dehydrogenation of formic acid over Pd-B/C and Pd/C, revealing that significantly enhanced dehydrogenation of HCOOH can be achieved on the home-synthesized Pd-B/C[1-3]. B-doping in the Pd lattice can be attained during the reduction of a Pd(II) precusor from an aqueous solution using dimethylamine borane as the reducing agent and boron source[1]. The XRD result suggested the expansion of Pd lattice and the XPS result indicated the partial electron transfer from B to Pd [3], lowering down the d-band center of Pd, favoring the dehydrogenation pathway, as supported by latest DFT calculation by Studt and Norskov[4]. In situ ATR-IR spectroscopy on Pd-B/C and Pd/C was comparatively conducted in conditions mimicking hydrogen production or direct formic acid fuel cell, it is revealed that desired dehyrogenation pathway forming CO2 is enhanced accompanied with inhibited accumulation of CO poissoning specie on Pd-B/C [2-3]. Since both forward and backward conversions may involve the weakly adsorbed formate as an active intermediate, it is thus interesting to explore the use of Pd-B/C as the catalyst for electroreducing CO2 to form HCOOH. Indeed, our recent preliminary analysis on the products of CO2 electroreduction over Pd-B/C and Pd/C catalysts in a KHCO3 electrolyte indicates that the formation of HCOOH on Pd-B/C is greatly enhanced as compared to that on Pd/C. Acknowledgements ：Financial supports from NSFC (grant No. 21273046 and 21473039）and the 973 Program (No. 2015CB932303) of MOST are highly appreciated References ： [1] J.Y. Wang, Y.Y. Kang, H. Yang, and W.B. Cai, J. Phys. Chem. C , 113, 8366 (2009). [2] K. Jiang, K. Xu, S.Z. Zou, and W.B. Cai, J. Am. Chem. Soc., 136, 4861 (2014). [3] K. Jiang, J.F. Chang, H. Wang, S. Brimaud, W. Xing, R. J. Behm, and W.B. Cai , ACS Appl. Mater. Interfaces, 8, 7133(2016) [4] J. S.Yoo, Z.-J. Zhao, J. K. Nørskov, and F. Studt, ACS Catal., 5, 6579 (2015).