Prediction of occurrence of solidification cracking in weld metal

Kenji Shinozaki,Yamamoto Motomichi,Wen Peng,Tamura Tomoko

DOI: https://doi.org/10.1080/09507111003655325

2008-01-01

Welding International

Abstract:Keywords: solidification cracking in situ observationlaser weldinghot ductility curve3D heat conduction analysis3D high-temperature strain analysisbrittleness temperature range

What problem does this paper attempt to address?

Prediction of Solidification Cracking by In-situ Observation and 3D FEM-Analysis

Peng WEN,Kenji SHINOZAKI,Motomichi YAMAMOTO,Yasutaka SENDA,Tomoko TAMURA,Norio NEMOTO

DOI: https://doi.org/10.2207/qjjws.27.139s

2009-01-01

QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY

Abstract:This study is purposed to develop a systematic method for prediction of solidification cracking during laser welding by accurately obtaining the high temperature ductility and weld strain of weld metal. The U-type hot cracking test was carried out under various initial loads; solidification cracking behavior was in-situ observed by a high speed camera so that the critical strain, for the initiation of solidification crack, was measured precisely. With the critical strain and temperature history measured at the solidification crack, the high temperature ductility curve was achieved. Meanwhile, a three dimensional FEM-analysis was performed to obtain the detailed strain history at the crack initiation point during laser welding. In order to get the accurate strain history, it is necessary to obtain the accurate material properties of weld metal at the elevated temperature up to solidification temperature range. The FEM-analysis was carried out by using the obtained high temperature material properties, which were measured by a developed high temperature tensile test with in-situ observation. Therefore, it became possible to predict the occurrence of solidification cracking during laser welding accurately by using both of the detailed high temperature ductility curve measured experimentally and the strain history obtained by the 3D FEM-analysis.
Study on Solidification Cracking of Laser Dissimilar Welded Joints by Using In-Situ Observation and Numerical Simulation

Peng Wen,Motomichi Yamamoto,Yasutaka Senda,Tomoko Tamura,Kenji Shinozaki

DOI: https://doi.org/10.1007/bf03266738

IF: 2.1

2010-01-01

Welding in the World

Abstract:This study is aimed at developing a systematic method for evaluation and prediction of solidification cracking in laser dissimilar welded joints (laser DWJ). The initiation of solidification cracking was observed directly by using a high speed camera during U-type hot cracking testing while laser welding. The high temperature ductility curves were obtained based on the local critical strains of the solidification cracks, measured by investigating each frame of the observation film. The distribution of residual liquid metal during solidification was investigated by using both high magnification and in-situ observation. Moreover, material properties at the elevated temperatures were measured by using a developed tensile test. The weld strain during laser welding was calculated by 3D finite element analysis by using the material properties obtained. Consequently, all the results helped to provide a comprehensive understanding of solidification cracking in laser DWJ.
In-situ Observation of Solidification Cracking of Laser Dissimilar Welded Joints

Peng Wen,Kenji Shinozaki,Motomichi Yamamoto,Yasutaka Senda,Tomoko Tamura,Norio Nemoto

DOI: https://doi.org/10.2207/qjjws.27.134s

2010-01-01

QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY

Abstract:This study is purposed to develop an evaluation method of solidification cracking susceptibility for laser DWJ of different dilution ratios. By using U-type hot cracking test with in-situ observation, the critical strain for the initiation of solidification cracking was measured locally near the crack rather than the macro strain measured in most other hot cracking tests. Meanwhile, the temperature history during laser welding at the trailing region of the molten pool was measured experimentally. The high temperature ductility curve was achieved based on the above test results of the critical strain and the temperature history. The critical strain rate of temperature drop (CST) was used to evaluate the solidification cracking susceptibility. Moreover, the residual liquid metal at the solidification front during laser welding was observed directly by using in-situ observation with an optical microscope lens. Consequently, all the results showed that solidification cracking susceptibility is the highest when the ratio of Inconel600 takes up roughly 40% in the weld bead among the used Inconel600/SUS347 laser DWJ.
Evaluation of solidification cracking susceptibility during laser welding by in-situ observation method

温鹏 wen peng,荻崎贤二 shinozaki kenji,山本元道 yamamoto motomichi

DOI: https://doi.org/10.3788/CJL201138.0603005

2011-01-01

Abstract:The rapid cooling during laser welding can prompt the occurrence of solidification cracking, however, few study is found on systematic research of solidification cracking during laser welding. It is the key to accurately measure the critical strain and temperature of the crack in order to know solidification cracking susceptibility. By using U-type hot cracking test with in-situ observation method, the occurrence of solidification cracking is captured clearly by high-speed-high-magnification camera. With the in-situ observation method, the local critical strain of crack is measured by tracking the displacement of two reference points near the crack; the local temperature of crack is measured by inserting the thermocouple to the trailing edge of the weld pool. Local critical strains at different temperatures are obtained under different tensile loads in U-type hot cracking test. The high temperature ductility curve is achieved accurately.
Development of Evaluation Method for Solidification Cracking Susceptibility of Inconel600/SUS347 Dissimilar Laser Weld Metal by In-Situ Observation

K. Shinozaki,M. Yamamoto,A. Kawasaki,T. Tamura,P. Wen

DOI: https://doi.org/10.4028/www.scientific.net/msf.580-582.49

2008-01-01

Materials Science Forum

Abstract:This study was carried out on the development of the evaluation method for solidification cracking susceptibility of Inconel600/SUS347 dissimilar weld metals during laser welding. Some dissimilar weld metals which have different ratios of Inconel600/SUS347 were prepared by TIG welding and then were remelted on the U-type hot cracking tester by laser. Solidification cracking behavior during hot cracking test was observed by a high speed camera and the dynamic strain, close to the solidification crack, was evaluated. It appeared that local critical strain, for the initiation of solidification crack, was obtained by this strain measurement method. So the solidification cracking susceptibility could be directly evaluated based on the critical strain for different dissimilar joint. By using this method, it was discovered that solidification cracking occurred most easily when the ratio of Inconel600/SUS347 is 40%/60%, in the case of the Inconel600/SUS347 dissimilar laser welded joints.
High speed and high magnification in situ observation of residual liquid metal during laser welding process

Wen Peng,Shinozaki Kenji,Yamamoto Motomichi

IF: 1.797

2011-01-01

ACTA METALLURGICA SINICA

Abstract:Weld solidification cracking is resulted from the low ductility during solidification progress of weld metal,which is considered to be determined by the distribution of residual liquid metal at solidification front.Thus,the in situ observation of residual liquid metal during welding can give significant information of solidification progress and weld solidification cracking.Few reports have been found so far in this aspect though many in situ observation researches have been carried out in welding field,for example,the observation of droplet transfer,weld pool shape,weld plasma and phase transformation etc..In this paper,solidification behavior of residual liquid metal at the trailing edge of the weld molten pool was in situ observed directly during laser welding by using high speed camera and high magnification optical lens.The precipitation of columnar grain from the molten pool and the solidification of the residual liquid metal at the trailing edge of weld molten pool were recorded in detail by using the high speed video system.Meanwhile,the solidifying structures in solidification process were frozen and reserved to room temperature by using the liquid Sn quenching method during laser welding.The quantity and morphology of residual liquid metal in quenched samples were observed and compared with the in situ observation results.It was found that the in situ observed residual liquid metal was the initial part of the coexistence range of liquid and solid during solidification progress. The in situ observed existence range of residual liquid metal has correspondence with the solidification cracking susceptibility in accordance with the fan-shaped hot cracking test results for three different austenite stainless steels.Consequently,this research provides experimental basis for the relationship between residual liquid metal and solidification cracking susceptibility.It shows the possibility to develop an in situ observation method to directly evaluate solidification cracking susceptibility of different materials during welding process.
EXPERIMENTAL RESEARCH AND NUMERICAL SIMU- LATION OF SOLIDIFICATION CRACK DURING LASER WELDING OF RING STRUCTURE

Wen Peng,Shinozaki Kenji,Yamamoto Motomichi

DOI: https://doi.org/10.3724/sp.j.1037.2011.00174

IF: 1.797

2011-01-01

ACTA METALLURGICA SINICA

Abstract:The combined influence of metallurgical and mechanical factors on welding solidification cracking structure in laser welded ring was investigated by using both experiments and numerical simulation. It is found that solidification cracking is directly related with the overlap weld part. The microstructure was observed under OM, and the grain size was measured by EBSD observation. The grains in overlap weld part are much bigger than those in single weld part, winch results in falling of ductility during solidification. The temperature and strain changes of weld metal in solidification temperature range were calculated out by using 3D finite element analysis. Compared with the single weld part, the strain rate with temperature drop is lower in overlap weld part, i.e.; the mechanical driving force to solidification cracking is weaker in overlap weld part. Consequently, it is concluded that the low ductility caused by coarse grain results in the occurrence of solidification cracking in overlap weld part during laser welding of ring structure. This research not only helps to understand the mechanism of solidification cracking in more details, but also guides the study on prediction of solidification cracking occurrence.
Prediction of the influence of welding metal composition on solidification cracking of laser welded aluminum alloy

Ailin Deng,Hui Chen,Yingbo Zhang,Yan Liu,Xiaoyi Yang,Zhenlin Zhang,Bingxu Zhang,Dupeng He

DOI: https://doi.org/10.1016/j.mtcomm.2023.105556

IF: 3.8

2023-02-10

Materials Today Communications

Abstract:The crack length of laser welding 6082 aluminum alloy with three types of 5000 series aluminum alloy welding materials was compared by fishbone test method. It was found that ER5A06 welding material corresponds to the shortest crack length, indicating that the welding material composition has an impact on the welding crack and the crack susceptibility could be controlled by adjusting the welding material composition. Combined with SEM and EBSD, the crack morphology was observed and determined to be solidification cracking. Through EDS, EPMA and thermodynamic calculation, it is found that the main elements affecting solidification cracking are Al, Mg, Si and Cu. The cooling rate of the fusion zone was calculated according to the secondary dendrite arm spacing and welding composition. Compared with casting and arc welding, the laser welding aluminum alloy fusion zone has rapid cooling rate. Due to the rapid cooling rate, the T - fs curves of Al-Mg, Al-Si and Al-Cu binary alloys were calculated by commercial thermodynamic software Thermo-Calc. Furthermore, the cracking susceptibility index (CSI) of binary aluminum alloys were also calculated to determine the element content range of the cracking. To understand the element interaction, both the machine learning and computational thermodynamic methods were employed to predict the influence of multi-component welding metal on solidification cracking susceptibility. Based on the calculation results of solidification cracking susceptibility for binary aluminum alloys, a data set containing 45 groups of aluminum alloy components was established and set as the input dataset. The CSI values corresponding to the compositions in the data set were set as the target and the relationship "welding metal composition - CSI" was founded. Based on the Kriging model, the influence of welding metal composition on solidification cracking susceptibility and the components of most crack susceptible were obtained, which provides a basis for welding materials design.

materials science, multidisciplinary
In Situ Observation Method for Quantitative Evaluation of Solidification Phenomena and Solidification Cracks during Welding

kenji shinozaki,motomichi yamamoto,kohta kadoi,peng wen

DOI: https://doi.org/10.4028/www.scientific.net/MSF.782.3

2014-01-01

Materials Science Forum

Abstract:Solidification cracking during welding is very serious problem for practical use. Therefore, there are so many reports concerning solidification cracking. Normally, solidification cracking susceptibility of material is quantitatively evaluated using Trans-Varestraint test. On the other hand, local solidification cracking strain was tried to measure precisely using in-situ observation method, called MISO method about 30 years ago. Recently, digital high-speed video camera develops very fast and its image quality is very high. Therefore, we have started to observe solidification crack using in site observation method. In this paper, the local critical strain of a solidification crack was measured and the high temperature ductility curves of weld metals having different dilution ratios and different grain sizes to evaluate quantitatively the effects of dilution ratio and grain size on solidification cracking susceptibility by using an improved in situ observation method.
Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

Lifeng Gan,Baoyin Zhu,Chao Ling,Dongfeng Li,Esteban P. Busso

DOI: https://doi.org/10.1016/j.jmps.2024.105652

IF: 5.582

2024-04-18

Journal of the Mechanics and Physics of Solids

Abstract:This work investigates the heterogeneous deformation and failure of HR3C austenitic stainless steel welded joints at room and typical service temperatures. Such types of welded joints are widely used in the new generation of fossil fuel power stations and are known to suffer from premature high temperature failure. Observation of in-service failures revealed that cracks may nucleate either in the heat affected zone or in the weld metal. The main objective of this work is to identify the local microstructural conditions and stress–strain fields responsible for both ductile failure and micro-crack nucleation within the weldment at low and high temperatures, respectively. To that purpose, a novel multi-scale micromechanics-based modelling framework is proposed. It relies on representative weld microstructure models digitally reconstructed from EBSD measurements, and dislocation density-based crystal plasticity models to describe the behaviour of individual grains in each weld region. A novel thermo-dynamically consistent relation for the configuration stored energy per unit volume is derived from the crystal plasticity framework. The single crystal models are calibrated and validated from a combination of uniaxial tensile tests on cross-weld specimens using high resolution digital image correlation techniques, representative volume elements of the polycrystals at the macro-scale, as well as micropillar compression tests at the scale of the individual grains. Predictions of heterogeneous inelastic deformation fields within the weldment at both 22 °C and 665 °C, and of micropillar compression behaviour of the individual weld single crystal phases are consistent with experimental data. The experimentally observed ductile failure of the weld metal at room temperature is successfully predicted using a Gurson-type void nucleation, growth and coalescence constitutive model. The suitability of the stored strain energy density and the accumulated plastic strain as crack initiation/creep failure indicators is investigated. It was found that predicted creep lifetimes with either indicator were very similar, and that they were relatively accurate for low stress levels.

mechanics,materials science, multidisciplinary,physics, condensed matter
An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Dewen Zhou,Xiaowei Wang,Chunan Zhang,Tianyu Zhang,Heng Li,Yefeng Chen,Xiancheng Zhang,Jianming Gong,Shantung Tu

DOI: https://doi.org/10.1016/j.ijfatigue.2023.107802

IF: 5.489

2023-01-01

International Journal of Fatigue

Abstract:In the present work, a numerical simulation based on the crystal plasticity finite element (CPFE) method is conducted to capture the different mechanical responses and damage in different micro areas of the P92 steel welded joint at 650 degrees C. A robust Matlab-Abaqus-Python interactive parameter optimization procedure is proposed to identify the constitutive parameters for heat affected zone (HAZ). Good agreement between experimental and simulated stress-strain curves verifies the accuracy of the present approach. Three fatigue indicator parameters are incorporated into the CPFE to capture the damage distribution under low cycle fatigue (LCF) and creep-fatigue interaction (CFI) loadings. The damage accumulation at grain boundaries is observed in the FE simulation. The damage captured by the simulation under both LCF and CFI loadings shifted from HAZ to base zone.
ICONE19-43939 Phenomenological Evaluation of Laser-Irradiated Welding Processes with a Combined Use of Higher-Accuracy Experiments and Computational Science Methodologies : (5) Numerical Simulation of the Welding Processes with a Multi-Dimensional Multi-Physics Analysis Code SPLICE

Susumu Yamashita,Tomonori Yamada,Yukihiro Yonemoto,Tomoaki Kunugi,Toshiharu Muramatsu

DOI: https://doi.org/10.1299/jsmeicone.2011.19._icone1943_349

2011-01-01

Abstract:It is quite important that the establishing the welding and solidification processes, generation of the residual stress, in a laser welding for various reactor components. In order to standardize laser welding repair processes and controlling a residual stress which is induced by laser welding, we constructed the fully parallelized laser welding simulation code using one-fluid model (solid, liquid and gas phases are simultaneously calculated by one set of governing equations) and some advanced numerical models, e.g., VSIA (Volume and Surface Integrated Average) based CIP finite volume method for the discretization, the THINC/WLIC scheme for an accurate interface capturing and the robust and stable pressure Poisson equation solver, AMG preconditioned BiCGSTAB method. In the simulation, the base material is a pure aluminum which was included to the code as a physical parameter and we considered the surface tension force and its effect of a temperature gradient named Marangoni effect. As a result, reasonable results were obtained that is welding bead which is one of the representative behavior of a low power density laser welding and the appropriate shape of the vertical cross section of the molten pool. Therefore, the model can be applied to practical laser welding problems and contribute the standardization of a laser welding repair technology.
Hot Cracking of Resistance Spot Welded Magnesium Alloy

B. Lang,D. Q. Sun,Z. Z. Xuan,X. F. Qin

DOI: https://doi.org/10.2355/isijinternational.48.77

2008-01-01

ISIJ International

Abstract:Crack features of resistance spot welded magnesium alloy joint and effects of welding parameters on susceptibility of the joint to hot cracking have been investigated. In the spot welded joints, solidification cracking in weld nugget and liquation cracking in heat-affected zone (HAZ) were often observed. The formation of solidification cracking is related to low melting point liquid films between dendrites due to segregation of Al and Mn atoms and tensile stress developed during cooling. In HAZ, the grain boundary melting occurred and grain became coarser. The liquation cracking appears in HAZ just adjacent to weld nugget and may be induced by solidification cracking at the edge of weld nugget. The welding parameters (heat input) have an obvious effect on susceptibility of weld nugget to hot cracking. The results show that relatively high heat input (i.e. relatively high welding current, long welding time or low electrode force) increase the hot cracking tendency. It is favorable to select relatively low heat input for reducing susceptibility of spot welded magnesium alloy joint to hot cracking.
Effect of Welding Defects on Mechanical Properties of Welded Joints Subjected to Temperature

Min Yan,Zhen Guo,Chenfeng Li,Yi Liu,Xiangren Wang

DOI: https://doi.org/10.12989/scs.2021.40.2.193

2021-01-01

Abstract:Welding defects negatively affect the safety of steel structures. In fire, the steel connections with welding defects would fracture prematurely that cause the structure lose their fire resistance. However, the knowledge of effects of welding defects on welding connections at elevated temperature are still limit. This paper conducted steady-state tensile tests on butt welded specimens with artificial defects to investigate the effect of defects on the mechanical properties of butt welding at high temperatures. These effects on the evolution law of stress and strain, fracture strengths and extension abilities were discussed. The results show that the stress concentration caused by the defects in the welding zone reduced the yield strengths of the weldments at high-temperature, and the stress concentration induced brittle fracture occurring at the welding zone at high temperature with low levels and produced different failure modes. The extension abilities of the weldments at different temperatures were influenced by the defect levels significantly.
Fracture prediction in transverse fillet welded joints of high strength structural steel

Ming-Ming Ran,Ya-Chao Zhong,Yuan-Zuo Wang,Guo-Qiang Li,Feng Xiong,Qi Ge

DOI: https://doi.org/10.1016/j.jcsr.2021.107101

IF: 4.349

2022-02-01

Journal of Constructional Steel Research

Abstract:Due to the huge property difference between high strength structural (HSS) steels and mild steels after welding, mechanical behavior and failure mode of fillet welded joints of HSS steels should be studied further. Numerical simulations can provide increased insight into this topic. This paper concerns finite element simulations of component tests of two types transverse fillet welded joints of HSS steels: lap-welded transverse fillet welds and cruciform type transverse fillet welds. In order to investigate the influences of triaxial stress states on fracture ductility of weld metals, a series of tests on specimens with various initial geometries are carried out. By comparing three typical uncoupled fracture models (stress triaxiality-dependent ductile fracture model (VGM), Lode angle-dependent ductile fracture model (MSSM) and combination of stress triaxiality and Lode angle ductile fracture model (BWM)), BWM gives precious prediction of ductile fracture of weld metals. The behaviors in terms of load-displacement and failure modes of transverse fillet welds are all well captured by the numerical simulations with calibrated ductile fracture models. Specifically, the location of fracture initiation and propagation of cracks obtained from simulations are both identical with real responses.

construction & building technology,engineering, civil
Analysis of Thermal Elastic-Plastic Behavior of Metals during Welding by Finite Element Method

T. Yamakawa,Y. Ueda

DOI: https://doi.org/10.2207/QJJWS1943.42.567

Abstract:It is well known that welding produces thermal stresses which cause distortion of structures and residual stresses which influence buckling strength and brittle fracture strength of welded structures. Cold cracking of the weldment has beem investigated from a mechanical point of view with special attention paid to thermal stresses induced during the cooling stage of a welding thermal cycle.For a better analysis on these subjects, it is necessary to obtain more accurate information on the entire histories of stresses and strains to which the material is subjected during the process of welding. At the instant of welding, a limited portion of the welded joint such as the weldment and the base metal in its vicinity is heated to a very high temperature and therafetr cooled down to room temperature. The thermal cycle proceeds, the temperature distribution changes with time and the mechanical properties of the metals depend on temperature. In order to perform a more reliable analysis, the above mentioned factors should be taken into account. However, there are many difficulties in analysing theoretically practical models, including these effects, by classical methods, and there are only a few reports of their analysis based on simplified assumptions, such as regarding the problem as one dimensional problem or neglecting most of tempe-rature-dependent factors.The authors developed a method of theoretical analysis on this problem based on the finite element method, with consideration of the effects of changes in modulus of elasticity, yield stress and coefficient of expansion of the metal which are dependent on temperature under the assumption that problem is regarded as quasi-static, so that there is no interaction between temperature distribution and stress one. Accordingly, the temperature analysis is carried out independently before the stress analysis. As both analyses take incremental procedure, they can take into consideration of the effects of experience of the material before a stage at the following step of computation. if necessary, such as the rate of cooling on phase transformation, peak temperature on the mechanical properties, etc. in addition to the above mentioned temperature dependent properties. Examples of calculation given here are thermal stresses induced in butt welded joint under a moving electorode and local stresses and strains in RRC specimens during thermal cycle, and they show the usefulness of the method to general cases of welding.

Materials Science,Engineering
Numerical and experimental study on thermal-metallurgical-mechanical behavior of high-strength steel welded joint

Huanhuan Li,Wei Dai,Yu Huang,Wei Yan,Ruolin Wu,Dang Wang

DOI: https://doi.org/10.1016/j.optlastec.2024.110802

IF: 4.939

2024-03-14

Optics & Laser Technology

Abstract:The welding-induced residual stress is closely related to the mechanical properties of the welded joint, which can accelerate crack propagation and reduce the fatigue life of the welded joint. Therefore, a new composite heat source model based on the actual weld morphology was proposed to calculate the temperature field of high-strength steel single-pass full penetration laser welded joints. The solid-state phase transformation and precipitation hardening model were established based on the actual microstructure of welded joints for more accurately predict the residual stress. Four cases were designed to compare and analyze the influence mechanism of the interaction between solid-state phase transformation and precipitation hardening on the residual stress of welded joints. The solid-state phase transformation has a significant effect on the longitudinal and transverse stresses and stress evolution of welded joints. It increases the peak longitudinal compressive stress from –140.6 MPa to –755.1 MPa, with an increase of 529.52 %. Moreover, the longitudinal high stress gradient values generated at the junction of base metal and heat affected zone are as high as 860.9 MPa. Precipitation hardening behavior can weaken the peaks and high stress gradient values of transverse and longitudinal stresses. It can also make the longitudinal stress distribution of the fusion zone and the transverse stress distribution of the heat affected zone more homogeneous. In engineering applications, it was recommended that considering solid-state phase transformation in simulation calculation could accurately predict welding-induced residual stress without considering precipitation strengthening.

optics,physics, applied
Measurement of Local Material Properties and Failure Analysis of Resistance Spot Welds of Advanced High-Strength Steel Sheets

Yunwu Ma,Akira Takikawa,Jun Nakanishi,Kazuyoshi, Doira,Tetsuo Shimizu,Yongxin Lu,Ninshu Ma

DOI: https://doi.org/10.2139/ssrn.3772562

2021-01-01

SSRN Electronic Journal

Abstract:afety evaluation of resistance spot welds necessitates the accurate measurement of local constitutive properties. This study employed miniature mechanical tests to investigate the deformation and failure behaviors of nugget, heat affected zone (HAZ), and corona bond of resistance spot welded JSC980YL steel. A novel mini-peel test was developed to enable local fracture in HAZ for numerical inverse calibration of constitutive parameters. The fracture constants of weld zones calibrated using Cockcroft-Latham ductile failure criterion were incorporated in finite element models to predict the failure modes of spot welds in tensile-shear and cross-tension coupon tests. The result indicates that the ultimate tensile strengths of the nugget and the corona bond were 37.6% higher and 5.8 % lower, respectively, than that of the base material. The nugget and HAZ exhibited ductile fracture, whereas the corona bond was brittle fracture with only 1.2% elongation. In the coupon tests, the increase of nugget diameter slowed down the damage accumulation rate in the nugget and accelerated that in the HAZ, resulting in the transition of failure mode from interfacial to pullout. The failure load of corona bond in coupon tests increased with the increase of nugget diameter while its contribution to the peak load decreased.

English Else
A Study on Heat Input Control and a Quality Evaluation Algorithm to Prevent Toughness Deterioration of the Heat-Affected Zone in the Fiber Laser Welding Process of ASTM A553-1 (9% Nickel Steel) Material

Minho Park,Jaewoong Kim,Changmin Pyo

DOI: https://doi.org/10.3390/met12071195

IF: 2.695

2022-07-14

Metals

Abstract:Various international organizations and governments of many countries are making efforts to prevent environmental pollution, with the IMO (International Maritime Organization) reinforcing related regulations. With these regulations, equipment related to LNG-fueled ships, which have the greatest carbon dioxide reduction effect among eco-friendly ships, are expected to increase. Although the IGC code designates the materials that can be used for LNG containers, such as 304L stainless steel and 9% nickel steel, these materials have a tendency to deteriorate the tissue around the heat-affected zone due to excessive heat input. In this study, we analyzed the effect of brittle fracture in the weld zone and heat-affected zone after fiber laser welding and found that welding quality improved with control of the heat input. SVM discriminant analysis was applied to classify the groups in which brittle fracture and ductile fracture occurred. The shape of the penetration section, hardness in the welding zone and heat-affected zone, and fracture surface were selected as factors for discrimination; these values were determined under various welding conditions. With these data, we derived a regression model and multi-objective optimization algorithm to predict mechanical properties after welding, as well as the conditions necessary to prevent brittle fracture. Finally, the prediction models were verified, as the results of welding under the derived conditions were classified as ductile fracture group.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Effect of Inhomogeneous Mechanical Properties on the Stress-Strain Field at the Crack Tip and Crack Growth Direction in Dissimilar Metal Welded Joints

Shuang Wang,Hongkui Zhang,Zhe Ju,Bing Li,Fandong Chen,Fei Han

DOI: https://doi.org/10.1155/2023/6408667

IF: 0.849

2023-08-11

Science and Technology of Nuclear Installations

Abstract:In the failure analysis and safety assessment of dissimilar metal welded joints, the mechanical heterogeneity of local regions is usually ignored and limited sampling locations are selected. The mechanical behavior of the crack tip region is the main variables affecting the environmentally assisted cracking behavior, and it is crucial for understanding the impact of mechanical heterogeneity on the local stress-strain state at the crack tip in welded joints. In this study, the effect of mechanical heterogeneity on the local mechanical behavior at the crack tip and on the stress-strain condition at the crack tip front for different crack sizes was investigated through finite-element simulations based on user-defined material subroutines. The local mechanical behavior of an interface region and crack propagation direction with mechanical heterogeneity and a series of initial crack locations were analyzed. The results show that mechanical heterogeneity has a significant effect on the mechanical condition and growth path of cracks at different sampling locations. The interaction between the mechanical heterogeneity around the crack and the crack depth determines the stress and plastic strain in front of the crack tip, which causes a substantial change in the crack growth path. The interface cracks have high stress and plastic strain; thus, the interface is often the weak position where damage occurs. To guarantee a reliable integrity assessment of cracks in mechanically heterogeneous interface regions, local mechanical properties related to crack locations should be determined and utilized.

nuclear science & technology

Prediction of occurrence of solidification cracking in weld metal

Prediction of Solidification Cracking by In-situ Observation and 3D FEM-Analysis

Study on Solidification Cracking of Laser Dissimilar Welded Joints by Using In-Situ Observation and Numerical Simulation

In-situ Observation of Solidification Cracking of Laser Dissimilar Welded Joints

Evaluation of solidification cracking susceptibility during laser welding by in-situ observation method

Development of Evaluation Method for Solidification Cracking Susceptibility of Inconel600/SUS347 Dissimilar Laser Weld Metal by In-Situ Observation

High speed and high magnification in situ observation of residual liquid metal during laser welding process

EXPERIMENTAL RESEARCH AND NUMERICAL SIMU- LATION OF SOLIDIFICATION CRACK DURING LASER WELDING OF RING STRUCTURE

Prediction of the influence of welding metal composition on solidification cracking of laser welded aluminum alloy

In Situ Observation Method for Quantitative Evaluation of Solidification Phenomena and Solidification Cracks during Welding

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

ICONE19-43939 Phenomenological Evaluation of Laser-Irradiated Welding Processes with a Combined Use of Higher-Accuracy Experiments and Computational Science Methodologies : (5) Numerical Simulation of the Welding Processes with a Multi-Dimensional Multi-Physics Analysis Code SPLICE

Hot Cracking of Resistance Spot Welded Magnesium Alloy

Effect of Welding Defects on Mechanical Properties of Welded Joints Subjected to Temperature

Fracture prediction in transverse fillet welded joints of high strength structural steel

Analysis of Thermal Elastic-Plastic Behavior of Metals during Welding by Finite Element Method

Numerical and experimental study on thermal-metallurgical-mechanical behavior of high-strength steel welded joint

Measurement of Local Material Properties and Failure Analysis of Resistance Spot Welds of Advanced High-Strength Steel Sheets

A Study on Heat Input Control and a Quality Evaluation Algorithm to Prevent Toughness Deterioration of the Heat-Affected Zone in the Fiber Laser Welding Process of ASTM A553-1 (9% Nickel Steel) Material

Effect of Inhomogeneous Mechanical Properties on the Stress-Strain Field at the Crack Tip and Crack Growth Direction in Dissimilar Metal Welded Joints