Abstract:Past research has indicated that Calcium sulphoaluminate (CSA) cementitious materials show superior resistance against sulfate attack compared with Portland cement. For this study, the diffusion coefficients of sulfate ions in CSA cement mortar were analyzed using an alternating current (AC) impedance method in order to further disclose the mechanism of sulfate resistance in CSA cement. The results showed that the diffusion coefficients of sulfate ions in CSA mortars were close to those in Portland cement mortars, though a large number of sulfate ions had penetrated the specimen with no sulfate damage occurring when immersed for 240 days. It could therefore be confirmed that the better sulfate resistance of CSA cement was not responsible for the low permeability, but rather for the fact that no chemical interaction between hydration products and sulfates took place, and that no expansive products were formed. (C) 2019 Elsevier Ltd. All rights reserved.

Sulfate Diffusion in Calcium Sulphoaluminate Mortar