Effect of Ni on Microstructures and Mechanical Properties for Multielemental Nb–Si-Based Alloys
Chen, Dezhi,Wang, Qi,Chen, Ruirun,Zhou, Zhecheng,Su, Yanqing,Fu, Hengzhi
DOI: https://doi.org/10.1007/s11661-022-06634-0
2022-01-01
Metallurgical and Materials Transactions A
Abstract:Eight-element Nb–Si alloys (Nb–Si–Ti–Cr–Al–Hf–Zr–Ni) with different Ni contents were prepared by arc melting to obtain Nb–Si alloys with high mechanical properties. Phase selection, microstructure evolution, room-temperature fracture toughness, and compressive properties were investigated systematically. Results showed that the eutectic Nb–Si alloy becomes a hypereutectic Nb–Si alloy with the increase in Ni content. All alloys contain Nbss, γ -(Nb, X) 5 Si 3 and Cr 2 (Nb, X) phases, and 2Ni and 3Ni alloys also contain the primary α -(Nb, X) 5 Si 3 phase. With the increase in Ni content, the content and size of the primary α -(Nb, X) 5 Si 3 phase increased. K Q first increased and then decreased, with the highest K Q of 12.6 MPa m 1/2 occurring in the 2Ni alloy. The room-temperature maximum compressive strength was improved with 1 at. pct Ni addition but decreased with higher Ni addition. The strengthening mechanism is solid solution strengthening and a high content of the γ -(Nb, X) 5 Si 3 phase by Ni element addition.