Novel Bipolar Phenanthroimidazole Derivative Design for a Nondoped Deep‐Blue Emitter with High Singlet Exciton Yields
Miao Chen,Yi Yuan,Ji Zheng,Wen-Cheng Chen,Long-Ji Shi,Ze-Lin Zhu,Feng Lu,Qing-Xiao Tong,Qing-Dan Yang,Jun Ye,Mei-Yee Chan,Chun-Sing Lee
DOI: https://doi.org/10.1002/adom.201500258
IF: 9
2015-01-01
Advanced Optical Materials
Abstract:phenanthro[9,10d ]imidazole (PI) chromophore. PI is a deepblue emitting chromophore with an interesting property that it can behave respectively as a mild donor or acceptor depending on whether it is linked at the N1 or the C2 positions (Figure 1 ). Here, the two fl uorescence enhancement approaches are simultaneously implemented for the fi rst time by jointing two identical PI chromophores via a biphenyl bridge at their N1 and C2 positions respectively. As expected, the emitters developed here do show high fl uorescent quantum yields and bipolar transporting properties. On the other hand, as the PI moieties behave only as a mild donor or acceptor, this endows the designed molecules with suitable amounts of ICT which do not cause signifi cant spectral redshifts. As a results, the two emitters, 1-(4-( tert -butyl) phenyl)-2-(4′-(2-(4-( tert -butyl)phenyl)1 H -phenanthro[9,10d ]imidazol-1-yl)-[1,1′-biphenyl]-4-yl)-1 H phenanthro[9,10d ]imidazole (4nPI-BP-4PI) and 1-(4-( tert -butyl) phenyl)-2-(3′-(2-(4-( tert -butyl)phenyl)-1 H -phenanthro[9,10d ] imidazol-1-yl)-[1,1′-biphenyl]-4-yl)-1 H -phenanthro[9,10d ]imidazole (3nPI-BP-4PI), developed in this work show deep-blue emissions, high fl uorescent yields and bipolar transporting properties. Blue emissions from the OLEDs prepared with the two compounds (CIE coordinates: 4nPI-BP-4PI:(0.15, 0.08), 3nPI-BP-4PI:(0.15, 0.06)) are close to the NTSC standard (CIE:0.14, 0.08) and show external quantum effi ciencies (EQE) (4nPI-BP-4PI:5.56% and 3nPI-BP-4PI:4.95%) around the theoretical limit of about 5% for fl uorescent OLEDs without any photon extraction layer. The present devices show effi ciencies comparable to the best reported deep-blue OLEDs with CIEy coordinate below 0.08. Synthesis routes for 4nPI-BP-4PI and 3nPI-BP-4PI are summarized in Scheme S1 (Supporting Information). In the synthesis, commercially available raw chemicals were reacted in an argon atmosphere and the products were separated with good yields. Molecular structures of the products were determined with 1 H NMR and mass spectroscopy. Thermal properties of the new compounds were investigated with thermogravimetric analysis and differential scanning calorimetry under a nitrogen atmosphere (Figures S1, Supporting Information). As shown the Table 1 , both 4nPI-BP-4PI and 3nPI-BP-4PI are thermally stable with decomposition temperatures ( T d ) (5% weight loss) of 525 and 536 °C, respectively. Glass-transition temperature ( T g ) of 3nPI-BP-4PI was found to be 192 °C while that of 4nPIBP-4PI could not be observed. Figure 2 shows absorption spectra of the two emitters in dilute (dichloromethane) DCM solutions as well as their M. Chen, J. Zheng, L.-J. Shi, Z.-L. Zhu, F. Lu, Prof. Q.-X. Tong Department of Chemistry and Key laboratory for Perparation and Application of Ordered Structural Materials of Guangdong Province Shantou University Guangdong 515063 , China E-mail: qxtong@stu.edu.cn Y. Yuan, W.-C. Chen, Dr. Q.-D. Yang, Dr. J. Ye, Prof. C.-S. Lee Center of Super-Diamond and Advanced Films (COSDAF) and Department of Physics and Materials Science City University of Hong Kong Hong Kong SAR , China E-mail: apcslee@cityu.edu.hk Dr. M.-Y. Chan Department of Chemistry The University of Hong Kong Pokfulam Road , Hong Kong Novel Bipolar Phenanthroimidazole Derivative Design for a Nondoped Deep-Blue Emitter with High Singlet Exciton Yields