Ultrahigh power density and energy storage density of Ti-free Ca-doped (Pb,La) (Zr,Sn)TaO3 antiferroelectric ceramics
Han Zhao,Ran Xu,Meng Jiao Wang,Xiao Zhi Wang,Qing Shan Zhu,Zhuo Xu
DOI: https://doi.org/10.1039/d3tc02198j
IF: 6.4
2023-08-24
Journal of Materials Chemistry C
Abstract:Antiferroelectric ceramics have attracted much attention for application in pulsed power systems due to their high discharge energy density and energy storage density. There is no easily reduced Ti 4+ in (Pb,La) (Zr,Sn)O 3 -based antiferroelectric, which is beneficial for the preparation of low-cost ceramic capacitors by co-sintering with base metals as dielectric materials in a reducing atmosphere. However, in (Pb,La) (Zr,Sn)O 3 -based antiferroelectric ceramics, it is difficult to achieve more than 90% energy storage efficiency due to the existence of secondary phase transition. Here, the oxygen vacancy is compensated by Ta 5+ to increase the domain flipping, and the relaxation degree is increased by Ca 2+ to improve the energy storage efficiency. The energy storage efficiency, energy storage density and discharge energy density are effectively improved by co-doping Pb 0.98− x La 0.02 Ca x (Zr 0.6 Sn 0.4 ) 0.97 Ta 0.02 O 3 ( x = 0, 0.005, 0.01, and 0.015) with Ta 5+ and Ca 2+ . The energy storage efficiency of all components is above 90%. Among them, Pb 0.97 La 0.02 Ca 0.01 (Zr 0.6 Sn 0.4 ) 0.97 Ta 0.02 O 3 exhibited a high recoverable energy density ( W rec = 7.93 J cm −3 ) and an excellent energy storage efficiency ( η = 93.9%) at 300 kV cm −1 . In addition, the ceramic exhibited a high discharge energy density ( W dis = 6.28 J cm −3 ), a high power density ( P D = 276.9 MW cm −3 ), and a fast discharge rate ( t 0.9 = 287 ns) at a relatively low electric field of 290 kV cm −1 . The above results indicate that Pb 0.97 La 0.02 Ca 0.01 (Zr 0.6 Sn 0.4 ) 0.97 Ta 0.02 O 3 is a potential candidate material for pulse capacitors.
materials science, multidisciplinary,physics, applied