Abstract:The catalytic conversion of dinitrogen (N-2) into ammonia under ambient conditions represents one of the Holy Grails in sustainable chemistry. As a potential alternative to the Haber-Bosch process, the electrochemical reduction of N-2 to NH3 is attractive owing to its renewability and flexibility, as well as its sustainability for producing and storing value-added chemicals from the abundant feedstock of water and nitrogen on earth. However, owing to the kinetically complex and energetically challenging N-2 reduction reaction (NRR) process, NRR electrocatalysts with high catalytic activity and high selectivity are rare. In this contribution, as a proof-of-concept, we demonstrate that both the NH3 yield and faradaic efficiency (FE) under ambient conditions can be improved by modification of the hematite nanostructure surface. Introducing more oxygen vacancies to the hematite surface renders an improved performance in NRR, which leads to an average NH3 production rate of 0.46 mu g h(-1) cm(-2) and an NH3 FE of 6.04 % at -0.9 V vs. Ag/AgCl in 0.10 m KOH electrolyte. The durability of the electrochemical system was also investigated. A surprisingly high average NH3 production rate of 1.45 mu g h(-1) cm(-2) and a NH3 FE of 8.28 % were achieved after the first 1 h chronoamperometry test. This is among the highest FEs reported so far for non-precious-metal catalysts that use a polymer-electrolyte-membrane cell and is much higher than the FE of precious-metal catalysts (e.g., Ru/C) under comparable reaction conditions. However, the NH3 yield and the FE dropped to 0.29 mu g h(-1) cm(-2) and 2.74 %, respectively, after 16 h of chronoamperometry tests, which indicates poor durability of the system. Our results demonstrate the important role that the surface states of transition-metal oxides have in promoting electrocatalytic NRR under ambient conditions. This work may spur interest towards the rational design of electrocatalysts as well as electrochemical systems for NRR, with emphasis on the issue of stability.

Electrochemical Synthesis of Ammonia Based on a Perovskite LaCrO3 Catalyst

LaNi0.2Cu0.8O3‐δ Perovskites as Electrocatalysts for Electro‐synthesis of Ammonia from Nitrogen Oxyanion

Highly Stable Perovskite Oxides for Electrocatalytic Acidic NOx− Reduction Streamlining Ammonia Synthesis from Air

A Perovskite La2Ti2O7nanosheet As an Efficient Electrocatalyst for Artificial N2fixation to NH3in Acidic Media

Electrochemical Synthesis of Ammonia by Zirconia-Based Catalysts at Ambient Conditions

Green synthesis of ammonia from steam and air using solid oxide electrolysis cells composed of ruthenium‐modified perovskite catalyst

Microfluidic-oriented Synthesis of Enriched Iridium Nanodots/carbon Architecture for Robust Electrocatalytic Nitrogen Fixation

Highly Selective Electrochemical Reduction Of Dinitrogen To Ammonia At Ambient Temperature And Pressure Over Iron Oxide Catalysts

Selective Electrochemical Reduction of Nitrogen to Ammonia by Adjusting the Three-Phase Interface

Recent progress and strategies on the design of catalysts for electrochemical ammonia synthesis from nitrate reduction

Recent Progress in the Electrochemical Ammonia Synthesis under Ambient Conditions

Efficient Electrocatalytic Properties of Transition Metal (mn, Co, Cu) Doped LaFeO3 for Ammonia Synthesis Via Nitrate Reduction

A Rare-Earth Samarium Oxide Catalyst for Electrocatalytic Nitrogen Reduction to Ammonia

Effects of AuCuB Catalysts with Porous Nanostructures on Electrosynthesis of Ammonia

Ammonia Synthesis via Electrochemical Nitrogen Reduction Reaction on Iron Molybdate under Ambient Conditions

Development of Electrocatalysts for Efficient Nitrogen Reduction Reaction under Ambient Condition

Heterogeneous crystalline–amorphous interface for boosted electrocatalytic nitrogen reduction to ammonia

Amorphous Sn/Crystalline SnS2 Nanosheets Via in Situ Electrochemical Reduction Methodology for Highly Efficient Ambient N2 Fixation.

Hierarchical Cobalt Phosphide Hollow Nanocages toward Electrocatalytic Ammonia Synthesis under Ambient Pressure and Room Temperature

High-Efficiency Electrosynthesis of Ammonia with High Selectivity under Ambient Conditions Enabled by VN Nanosheet Array

Ammonia Synthesis from Electrocatalytic N2 Reduction under Ambient Conditions by Fe2O3 Nanorods