Interfacial engineered Fe2O3@FeP nanorod arrays as capacitive storage dominated and high charge transfer anode for high-rate lithium-ion batteries
Jie Zheng,Ran Dong,Peng Liu,Xianqiang Peng,Wen Tian,Xingbin Lv,Shuai Tan,Junyi Ji
DOI: https://doi.org/10.1016/j.surfcoat.2021.127471
IF: 4.865
2021-09-01
Surface and Coatings Technology
Abstract:<p>The development of the promising anode material with high energy density, long lifespan, high safety, and low cost is essential for next-generation energy storage devices. Herein, the vertically aligned Fe<sub>2</sub>O<sub>3</sub>@FeP hybrid nanorod arrays anchored on carbon cloth (Fe<sub>2</sub>O<sub>3</sub>@FeP/CC) is successfully fabricated The FeP coating layer is <em>in-situ</em> transferred on the Fe<sub>2</sub>O<sub>3</sub> nanorod <em>via</em> phosphorization treatment, thus form an intimate contact interface with similar expansion coefficient. The FeP together with CC substrate can construct bi-continuous conductive networks to facilitate electron transfer and enhance structural robustness, while the open porous arrays and FeP with large bonding distance can promote electrolyte impregnation and Li<sup>+</sup> migration, thus effectively enhance the rate capability. Therefore, the Fe<sub>2</sub>O<sub>3</sub>@FeP/CC-8 electrode exhibits a superior reversible capacity of 2692 mAh g<sup>−1</sup> at 0.1 A g<sup>−1</sup>, remarkable cycling stability of 2232 mAh g<sup>−1</sup> after 100 cycles at 0.2 A g<sup>−1</sup>, and excellent rate capability of 1320 mAh g<sup>−1</sup> at 2.0 A g<sup>−1</sup>. Moreover, the surface capacitive dominated Li-storage mechanism and the high Li<sup>+</sup> diffusion coefficient (2.69 × 10<sup>−12</sup> cm<sup>2</sup> s<sup>−1</sup>) also verifies the fast ion/electron transfer kinetics. This simple but effective structural design and interface engineering strategy with high ion/electron transfer kinetics can be extended to general electrode design in many fields.</p>
physics, applied,materials science, coatings & films