Facile Preparation of Active Lignin Capsules for Developing Self-Healing and UV-blocking Polyurea Coatings

Yong Qian,Yijie Zhou,Lan Li,Weifeng Liu,Dongjie Yang,Xueqing Qiu

DOI: https://doi.org/10.1016/j.porgcoat.2019.105354

IF: 6.6

2020-01-01

Progress in Organic Coatings

Abstract:Aromatic skeleton and polyhydroxyl structure endow biomass lignin with excellent dispersibility, reactivity, and UV-blocking property. Herein, spherical microcapsules loaded with isophorone diisocyanate (IPDI) as core materials were prepared via interfacial polymerization in an oil-in-water emulsion, using sodium lignosulfonate (NaLS) as an emulsifier. Small amount of polydiphenylmethane diisocyanate (PMDI) was added to reinforce the shells of the capsules. The results show that the capsules were 43.4-118.3 mu m with a shell thickness of 1.9-2.5 mu m. The core fraction was approximately 72.6 wt% and the functional groups of IPDI, such as cyanates, were well preserved. The NaLS-based microcapsules were subsequently mixed and reacted with hexamethylene diisocyanate (HDI) and amine component successively to form new polyurea. When the new polyurea was coated on a steel substrate, it exhibited excellent self-healing property after being scratched. The healed polyurea presents nearly the same anticorrosion ability as the unscratched coating in a solution with high salt concentration. Moreover, the addition of NaLS-based capsules could effectively slow down the aging process of polyurea coatings. The color change of the self-healing polyurea leveled off after 200 h of UV irradiation, while retaining 40% of the breaking strength and 50% of elongation at break. Comparatively, the color of pure polyurea deepened continuously and the mechanical property disappeared completely.