Tunable oxygen vacancy concentration in vanadium oxide as mass-produced cathode for aqueous zinc-ion batteries

Yehong Du,Xinyu Wang,Juncai Sun

DOI: https://doi.org/10.1007/s12274-020-3109-x

IF: 9.9

2020-09-30

Nano Research

Abstract:<p class="a-plus-plus">Oxygen vacancy (Vö) is important in the modification of electrode for rechargeable batteries. However, due to the scarcity of suitable preparation strategy with controllable Vö incorporation, the impact of Vö concentration on the electrochemical performances remains unclear. Thus, in this work, Vö-V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>-PEDOT (VöVP) with tunable Vö concentration is achieved via a spontaneous polymerization strategy, with the capability of mass-production. The introduction of poly(2,3-dihydrothieno-1,4-dioxin) (PEDOT) not only leads to the formation of Vö in V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>, but it also results in a larger interlayer spacing. The as-prepared Vö-V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>-PEDOT-20.3% with Vö concentration of 20.3% (denoted as VöVP-20) is able to exhibit high capacity of 449 mAh·g<sup class="a-plus-plus">−1</sup> at current density of 0.2 A·g<sup class="a-plus-plus">−1</sup>, with excellent cyclic performance of 94.3% after 6,000 cycles. It is shown in the theoretical calculations that excessive Vö in V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> will lead to an increase in the band gap, which inhibits the electrochemical kinetics and charge conductivity. This is further demonstrated in the experimental results as the electrochemical performance starts to decline when Vö concentration increases beyond 20.3%. Thus, based on this work, scalable fabrication of high-performance electrode with tunable Vö concentration can be achieved with the proposed strategy. </p>

materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology

What problem does this paper attempt to address?

This paper attempts to address the issue of how to improve the electrochemical performance of vanadium oxide (V₂O₅) as a cathode material in aqueous zinc-ion batteries (ZIBs) by controlling the concentration of oxygen vacancies (Vö) in V₂O₅. Specifically, the study aims to develop a simple and scalable method to achieve V₂O₅-PEDOT composites with controllable oxygen vacancy concentrations and to explore the impact of different oxygen vacancy concentrations on electrochemical performance.

### Main Issues:
1. **How to achieve controllable oxygen vacancy concentration**: Existing preparation methods are complex and difficult to scale up, and precisely controlling the oxygen vacancy concentration is also a major challenge.
2. **Impact of oxygen vacancy concentration on electrochemical performance**: It is currently unclear how different concentrations of oxygen vacancies specifically affect electrochemical performance, especially whether too high a concentration of oxygen vacancies will lead to a decline in electrochemical performance.

### Solution:
- **Spontaneous polymerization strategy**: By mixing commercial V₂O₅ with EDOT monomer at room temperature, in-situ polymerization of PEDOT is achieved while forming oxygen vacancies in the V₂O₅ lattice. By adjusting the amount of EDOT monomer, the concentration of oxygen vacancies can be controlled.
- **Performance testing and theoretical calculations**: Electrochemical tests (such as cyclic voltammetry, constant current charge-discharge, etc.) and density functional theory (DFT) calculations are used to evaluate the electrochemical performance at different oxygen vacancy concentrations.

### Experimental Results:
- **Optimal oxygen vacancy concentration**: Experimental results show that when the oxygen vacancy concentration is 20.3%, the V₂O₅-PEDOT composite exhibits the highest specific capacity (449 mAh·g⁻¹) and excellent cycling stability (capacity retention rate of 94.3% after 6,000 cycles).
- **Excessive oxygen vacancy concentration**: When the oxygen vacancy concentration exceeds 20.3%, the electrochemical performance begins to decline, which is consistent with theoretical calculation results, indicating that too high an oxygen vacancy concentration leads to an increase in band gap, thereby inhibiting electrochemical kinetics and charge conduction.

### Conclusion:
The developed spontaneous polymerization strategy enables the scalable production of V₂O₅-PEDOT composites with controllable oxygen vacancy concentrations, significantly improving the electrochemical performance of aqueous zinc-ion batteries. This method is not only simple and feasible but also allows precise control of oxygen vacancy concentration by adjusting the amount of EDOT monomer, providing new insights for the design of high-performance cathode materials.