Amphoteric-side-chain Functionalized "Ether-free" Poly(arylene piperidinium) Membrane for Advanced Redox Flow Battery.

Xiaoming Yan,Huaqing Zhang,Zhongyue Hu,Lv Li,Lei Hu,Zhiang Li,Li Gao,Yan Dai,Xigao Jian,Gaohong He

DOI: https://doi.org/10.1021/acsami.9b15872

IF: 9.5

2019-01-01

ACS Applied Materials & Interfaces

Abstract:To solve the stability issue of cost-effective non-fluorinated membranes, a ether-free poly(arylene piperidinium) (PBPip) based membrane is first applied in redox flow batteries (RFBs). For improved efficiencies of RFB, amphoteric side chains are introduced onto the PBPip. Without ether bond in the polymer backbone, the membrane shows a good stability in the strong oxidation environment. The FTIR spectra exhibit no obvious changes for 30 days of oxidation test. Different from traditional blended amphoteric membranes, the amphoteric side chain allows that cation and anion exchange capacities both increase with grafting degree, which leads to a very high total IEC (4.19 mmol g-1). Outstanding ion conduction ability (area resistance: 0.22 Ω cm2) comparable to Nafion 212 (0.24 Ω cm2) is consequently achieved. Ionic crosslinking structure between cationic and anionic groups results in low swelling rate (13.9%). Combining with repelling effect of positively charged piperidinium, a low VO2+ permeability (1.31×10-8 cm2 s-1) is accomplished. On the basis of these good properties, the membrane exhibits excellent vanadium battery performances, especially at high current densities. The VE and EE both exceeds 80% even at 200 mA cm-2. The battery performances have no obvious reductions after 500 cycles. These results indicate that this work provides a new orientation to design the membrane for RFB.