Piezoresistivity deterioration of smart graphene nanoplate/cement-based sensors subjected to sulphuric acid attack
Wenkui Dong,Wengui Li,Kirk Vessalas,Xuzhen He,Zhihui Sun,Daichao Sheng
DOI: https://doi.org/10.1016/j.coco.2020.100563
IF: 8
2021-02-01
Composites Communications
Abstract:<p>Intelligent cement-based sensors with self-sensing capacity have been explored for structural health monitoring (SHM) on the intrinsic piezoresistive performance. However, few studies had studied the piezoresistivity degradation of cement-based sensors after exposure to the aggressive environments, especially under sulphate acid attacks. In this study, graphene nanoplate (GNP)/cementitious composites were immersed in sulphuric acid solutions (concentrations of 0, 1%, 2%, and 3%) for 90 and 180 days. Then surface appearance, weight loss, mechanical properties, piezoresistivity and microstructure were investigated and compared the before and after sulphuric acid immersion. It was found that after acid immersion, the surface deterioration and mass loss were increased, and the compressive strength significantly was decreased. As for the intact GNP/cementitious composite, the piezoresistivity exhibited excellent linearity and repeatability, demonstrating the great potential to act as intelligent cement-based sensors for SHM. After 90 and 180 days of acid immersion, the piezoresistivity seemed sensitive to the initial low load initially but then to be less sensitive to the later high load. The highly corroded GNP/cementitious composites exhibited porous microstructures associated with the low compressive strength. The fractional changes to resistivity (FCR) under the low load could be attributed to the compressed pores and voids filled with erosion products that can form conductive passages. In contrast, with the increase of applied load, the intact cement matrix became much denser, which in turn constrained the further development of conductive passages in the GNP/cementitious composites.</p>
materials science, composites