Layer-by-Layer Assembly of Ultrathin Composite Films from Micron-Sized Graphite Oxide Sheets and Polycations
Nina I. Kovtyukhova,Patricia J. Ollivier,Benjamin R. Martin,Thomas E. Mallouk,Sergey A. Chizhik,Eugenia V. Buzaneva,Alexandr D. Gorchinskiy
DOI: https://doi.org/10.1021/cm981085u
IF: 10.508
1999-01-28
Chemistry of Materials
Abstract:Unilamellar colloids of graphite oxide (GO) were prepared from natural graphite and were grown as monolayer and multilayer thin films on cationic surfaces by electrostatic self-assembly. The multilayer films were grown by alternate adsorption of anionic GO sheets and cationic poly(allylamine hydrochloride) (PAH). The monolayer films consisted of 11−14 Å thick GO sheets, with lateral dimensions between 150 nm and 9 μm. Silicon substrates primed with amine monolayers gave partial GO monolayers, but surfaces primed with Al13O4(OH)24(H2O)12 7+ ions gave densely tiled films that covered approximately 90% of the surface. When alkaline GO colloids were used, the monolayer assembly process selected the largest sheets (from 900 nm to 9 μm) from the suspension. In this case, many of the flexible sheets appeared folded in AFM images. Multilayer (GO/PAH) n films were invariably thicker than expected from the individual thicknesses of the sheets and the polymer monolayers, and this behavior is also attributed to folding of the sheets. Multilayer (GO/PAH) n and (GO/polyaniline) n films grown between indium−tin oxide and Pt electrodes show diodelike behavior, and higher currents are observed with the conductive polyaniline-containing films. The resisitivity of these films is decreased, as expected, by partial reduction of GO to carbon.
materials science, multidisciplinary,chemistry, physical