Novel Luminescence Enhancement and Splitting of Excitation and Emission Bands of Na2SiF6:Mn4+,Li+ Phosphors Induced by Li+ Co-Doping

Youmiao Liu,Yuelan Li,Jianming Meng,Weifeng Liang,Wenjing Huang,Sen Liao,Yingheng Huang,Huaxin Zhang

DOI: https://doi.org/10.1016/j.jlumin.2019.116770

IF: 3.6

2020-01-01

Journal of Luminescence

Abstract:In this paper, a series of novel Na2SiF6:Mn4+,Li+ (NSF:0.05Mn(4+), xLi(+)) phosphors were prepared with the cation exchange method. Some novel luminescent properties inducing by doping Li+ were observed: First, the striking thing is that the excitation (PLE) & emission (PL) intensities of Li+-doped sample (NSF:0.05Mn(4+), 0.08Li(+)) are 11.7 times higher than those of NSF:0.05Mn(4+); Second, when the concentration of Li+ >= 20%: (a) transition of (4)A(2g) -> T-4(2g) in excitation band and zero phonon line (ZPL), s-v(4) in emission band are all split into two peaks, respectively; (b) the peak intensities of as-v(6), ZPL, v(6) and v(4) in emission band are almost the same. The mechanism of these phenomena was discussed. The color purity, crystal-field, nephelauxetic effect, the critical distance and the multipolar interaction for the samples were determined. Besides, the optimal sample (NSF:0.05Mn(4+), 0.08Li(+)) has an excellent QY, which is as high as 99.83%. Good warm white light with low correlated color temperature (CCT = 4362 K) and high color rendering index (Ra = 88.5) was obtained from prototype WLEDs using the mixing phosphors of the optimal sample and YAG:Ce3+ on InGaN chip under a 20 mA drive current, making the optimal sample has potential application for blue light-based warm WLEDs.